IS 1570 (Part 4) 60Cr4V2 vs IS 5517 58Cr4V1

Strong Match — 86.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 60Cr4V2 (IS 1570 (Part 4):1988) and IS 5517 58Cr4V1 (IS 5517:1993) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 60Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 5517 58Cr4V1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 60Cr4V2 vs IS 5517 58Cr4V1 is a 86.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.9%.

Frequently Compared With IS 1570 (Part 4) 60Cr4V2:
EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5
Match Breakdown
CHEMISTRY MATCH
86.9%
MECHANICAL MATCH
No shared data
OVERALL
86.9%
Specifications
Property IS 1570 (Part 4) 60Cr4V2 IS 5517 58Cr4V1
Standard IS 1570 (Part 4):1988 IS 5517:1993
Category Alloy Steel Alloy Steel
C (%) 0.55-0.65 0.53-0.63
Si (%) 0.10-0.35 0.15-0.50
Mn (%) 0.80-1.10 0.80-1.10
Cr (%) 0.90-1.20 0.90-1.20
V (%) >=0.15 0.07-0.12
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 60Cr4V2 IS 5517 58Cr4V1
Tensile Strength Not specified 980-1180 MPa
Yield Strength (0.2% proof) Not specified 735 MPa min
Elongation Not specified >=12%
Izod Impact Not specified 41 J min
Hardness (annealed) Not specified <=250 HB
Condition Not specified Hardened and tempered, ruling section up to 250 mm
Key Differences
Can IS 1570 (Part 4) 60Cr4V2 Be Substituted With IS 5517 58Cr4V1?
IS 1570 (Part 4) 60Cr4V2 and IS 5517 58Cr4V1 overlap closely enough on chemistry and mechanical properties that IS 5517 58Cr4V1 is often considered as a substitute for IS 1570 (Part 4) 60Cr4V2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 4) 60Cr4V2
0 active listings and RFQs →
IS 5517 58Cr4V1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 60Cr4V2 and IS 5517 58Cr4V1?
IS 5517 58Cr4V1 specifies S, P which are not specified for IS 1570 (Part 4) 60Cr4V2.
Can IS 1570 (Part 4) 60Cr4V2 be substituted with IS 5517 58Cr4V1?
IS 1570 (Part 4) 60Cr4V2 and IS 5517 58Cr4V1 overlap closely enough on chemistry and mechanical properties that IS 5517 58Cr4V1 is often considered as a substitute for IS 1570 (Part 4) 60Cr4V2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.