IS 1570 (Part 5) X04Cr12 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr12 (IS 1570 (Part 5):1985) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr12 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X04Cr12 vs GOST 5632 08X18H10 is a 68% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X04Cr12:
EN 10088-1 1.4301 GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
68%
MECHANICAL MATCH
33.3%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X04Cr12 GOST 5632 08X18H10
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 ≤0.08
Si (%) <=1.0 ≤0.80
Mn (%) <=1.0 ≤2.00
P (%) <=0.040 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 11.5-13.5 17.0–19.0
Ni (%) Not specified 9.0–11.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr12 GOST 5632 08X18H10
Tensile Strength >=415 MPa ≥520 MPa
Yield Strength >=205 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=22.0% (50 mm) ≥40%
Hardness <=183 HB; <=88 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr12
Not documented
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 5) X04Cr12 Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 5) X04Cr12 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X04Cr12
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 5) X04Cr12
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr12 and GOST 5632 08X18H10?
GOST 5632 08X18H10 specifies Ni which is not specified for IS 1570 (Part 5) X04Cr12.
Can IS 1570 (Part 5) X04Cr12 be substituted with GOST 5632 08X18H10?
IS 1570 (Part 5) X04Cr12 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.