IS 1570 (Part 5) X04Cr17Ni12Mo2Ti vs ASTM A959 16-8-2H

Related Material — 65.1% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr17Ni12Mo2Ti (IS 1570 (Part 5):1985) and ASTM A959 16-8-2H (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr17Ni12Mo2Ti is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 16-8-2H is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X04Cr17Ni12Mo2Ti vs ASTM A959 16-8-2H is a 65.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.1%.

Frequently Compared With IS 1570 (Part 5) X04Cr17Ni12Mo2Ti:
EN 10088-1 1.4301 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 GOST 5632 08X18H10 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
65.1%
MECHANICAL MATCH
No shared data
OVERALL
65.1%
Specifications
Property IS 1570 (Part 5) X04Cr17Ni12Mo2Ti ASTM A959 16-8-2H
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.05-0.10
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 14.5-16.5
Ni (%) 10.0-14.0 7.5-9.5
Mo (%) 2.0-3.0 1.50-2.00
Ti (%) <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr17Ni12Mo2Ti ASTM A959 16-8-2H
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
Not documented
ASTM A959 16-8-2H
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 5) X04Cr17Ni12Mo2Ti Be Substituted With ASTM A959 16-8-2H?
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti
0 active listings and RFQs →
ASTM A959 16-8-2H
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A959 16-8-2H?
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti specifies Ti which is not specified for ASTM A959 16-8-2H.
Can IS 1570 (Part 5) X04Cr17Ni12Mo2Ti be substituted with ASTM A959 16-8-2H?
IS 1570 (Part 5) X04Cr17Ni12Mo2Ti and ASTM A959 16-8-2H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.