Post Stock Login Register

IS 1570 (Part 5) X04Cr18Ni10Nb vs IS 1570 (Part 5) X04Cr18Ni10Ti

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr18Ni10Nb (IS 1570 (Part 5):1985) and IS 1570 (Part 5) X04Cr18Ni10Ti (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr18Ni10Nb is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 5) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X04Cr18Ni10Nb vs IS 1570 (Part 5) X04Cr18Ni10Ti is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 5) X04Cr18Ni10Nb:
EN 10088-1 1.4006 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 12Kh13 ASTM A959 .- GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 1570 (Part 5) X04Cr18Ni10Nb IS 1570 (Part 5) X04Cr18Ni10Ti
Standard IS 1570 (Part 5):1985 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Nb (%) >=10xC, <=1.0 Not specified
Ti (%) Not specified >=5xC, <=0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr18Ni10Nb IS 1570 (Part 5) X04Cr18Ni10Ti
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=205 MPa (0.2 % proof stress)
Elongation >=40% (50 mm) >=40% (50 mm)
Hardness <=183 HB; <=88 HRB <=183 HB; <=88 HRB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Key Differences
Can IS 1570 (Part 5) X04Cr18Ni10Nb Be Substituted With IS 1570 (Part 5) X04Cr18Ni10Ti?
IS 1570 (Part 5) X04Cr18Ni10Nb and IS 1570 (Part 5) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Ti is often considered as a substitute for IS 1570 (Part 5) X04Cr18Ni10Nb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X04Cr18Ni10Nb
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr18Ni10Ti
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr18Ni10Nb and IS 1570 (Part 5) X04Cr18Ni10Ti?
IS 1570 (Part 5) X04Cr18Ni10Nb specifies Nb which is not specified for IS 1570 (Part 5) X04Cr18Ni10Ti. IS 1570 (Part 5) X04Cr18Ni10Ti specifies Ti which is not specified for IS 1570 (Part 5) X04Cr18Ni10Nb.
Can IS 1570 (Part 5) X04Cr18Ni10Nb be substituted with IS 1570 (Part 5) X04Cr18Ni10Ti?
IS 1570 (Part 5) X04Cr18Ni10Nb and IS 1570 (Part 5) X04Cr18Ni10Ti overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr18Ni10Ti is often considered as a substitute for IS 1570 (Part 5) X04Cr18Ni10Nb in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.