IS 1570 (Part 5) X04Cr18Ni10Ti vs EN 10088-1 X6CrNiNb18-10

Strong Match — 98.6% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr18Ni10Ti (IS 1570 (Part 5):1985) and EN 10088-1 X6CrNiNb18-10 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr18Ni10Ti is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6CrNiNb18-10 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X04Cr18Ni10Ti vs EN 10088-1 X6CrNiNb18-10 is a 98.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.6%.

Frequently Compared With IS 1570 (Part 5) X04Cr18Ni10Ti:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 12Kh13 ASTM A959 .- EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
No shared data
OVERALL
98.6%
Specifications
Property IS 1570 (Part 5) X04Cr18Ni10Ti EN 10088-1 X6CrNiNb18-10
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Cr (%) 17.0-19.0 17.0-19.0
Ni (%) 9.0-12.0 9.0-12.0
Ti (%) >=5xC, <=0.80 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr18Ni10Ti EN 10088-1 X6CrNiNb18-10
Tensile Strength >=515 MPa Not specified
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=183 HB; <=88 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Key Differences
Can IS 1570 (Part 5) X04Cr18Ni10Ti Be Substituted With EN 10088-1 X6CrNiNb18-10?
IS 1570 (Part 5) X04Cr18Ni10Ti and EN 10088-1 X6CrNiNb18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiNb18-10 is often considered as a substitute for IS 1570 (Part 5) X04Cr18Ni10Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X04Cr18Ni10Ti
0 active listings and RFQs →
EN 10088-1 X6CrNiNb18-10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr18Ni10Ti and EN 10088-1 X6CrNiNb18-10?
IS 1570 (Part 5) X04Cr18Ni10Ti specifies Ti which is not specified for EN 10088-1 X6CrNiNb18-10.
Can IS 1570 (Part 5) X04Cr18Ni10Ti be substituted with EN 10088-1 X6CrNiNb18-10?
IS 1570 (Part 5) X04Cr18Ni10Ti and EN 10088-1 X6CrNiNb18-10 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6CrNiNb18-10 is often considered as a substitute for IS 1570 (Part 5) X04Cr18Ni10Ti in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.