IS 1570 (Part 5) X04Cr19Ni13Mo3 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr19Ni13Mo3 (IS 1570 (Part 5):1985) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr19Ni13Mo3 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X04Cr19Ni13Mo3 vs GOST 5632 08X18H10 is a 62.6% match. As per mechanical properties, the match is 33.3%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X04Cr19Ni13Mo3:
EN 10088-1 1.4845 GOST 5632 12Kh13 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
62.6%
MECHANICAL MATCH
33.3%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 GOST 5632 08X18H10
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 ≤0.08
Si (%) <=1.0 ≤0.80
Mn (%) <=2.0 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 18.0-20.0 17.0–19.0
Ni (%) 11.0-15.0 9.0–11.0
Mo (%) 3.0-4.0 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 GOST 5632 08X18H10
Tensile Strength >=515 MPa ≥520 MPa
Yield Strength >=205 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=35% (50 mm) ≥40%
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X04Cr19Ni13Mo3
Not documented
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X04Cr19Ni13Mo3
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 5) X04Cr19Ni13Mo3
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr19Ni13Mo3 and GOST 5632 08X18H10?
IS 1570 (Part 5) X04Cr19Ni13Mo3 specifies Mo which is not specified for GOST 5632 08X18H10.
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 be substituted with GOST 5632 08X18H10?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.