IS 1570 (Part 5) X108Cr17Mo vs GOST 5632 06Kh23N28

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X108Cr17Mo (IS 1570 (Part 5):1985) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X108Cr17Mo is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X108Cr17Mo vs GOST 5632 06Kh23N28 is a 55.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X108Cr17Mo:
GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 08X18H10 EN 10088-1 1.4006 GOST 5632 12Kh13 IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
55.3%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X108Cr17Mo GOST 5632 06Kh23N28
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 ≤0.06
Si (%) <=1.0 ≤0.80
Mn (%) <=1.0 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 16.0-18.0 22.0–25.0
Ni (%) <=0.50 26.0–29.0
Mo (%) <=0.75 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X108Cr17Mo GOST 5632 06Kh23N28
Hardness <=269 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Tensile Strength Not specified ≥510 MPa
Yield Strength Not specified ≥196 MPa
Elongation Not specified ≥35%
Max Service Temp Not specified 1050°C
Typical Applications
IS 1570 (Part 5) X108Cr17Mo
Not documented
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
Can IS 1570 (Part 5) X108Cr17Mo Be Substituted With GOST 5632 06Kh23N28?
IS 1570 (Part 5) X108Cr17Mo and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X108Cr17Mo
No active listings currently.
GOST 5632 06Kh23N28
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 3100–3400 mm (122.05–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X108Cr17Mo
0 active listings and RFQs →
GOST 5632 06Kh23N28
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X108Cr17Mo and GOST 5632 06Kh23N28?
IS 1570 (Part 5) X108Cr17Mo specifies P, S, Mo which are not specified for GOST 5632 06Kh23N28.
Can IS 1570 (Part 5) X108Cr17Mo be substituted with GOST 5632 06Kh23N28?
IS 1570 (Part 5) X108Cr17Mo and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.