IS 1570 (Part 5) X10Cr17Mn6Ni4 vs GOST 5632 12Kh13

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X10Cr17Mn6Ni4 (IS 1570 (Part 5):1985) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X10Cr17Mn6Ni4 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X10Cr17Mn6Ni4 vs GOST 5632 12Kh13 is a 65.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X10Cr17Mn6Ni4:
ASTM A959 201 EN 10088-1 1.4845 ASTM A959 202 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
65.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X10Cr17Mn6Ni4 GOST 5632 12Kh13
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.20 0.09–0.15
Si (%) <=1.0 ≤0.80
Mn (%) 4.0-8.0 ≤0.80
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 16.0-18.0 12.0–14.0
Ni (%) 3.5-5.5 ≤0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X10Cr17Mn6Ni4 GOST 5632 12Kh13
Tensile Strength >=515 MPa ≥540 MPa (annealed)
Yield Strength >=275 MPa (0.2 % proof stress) Not specified
Elongation >=40% (50 mm) Not specified
Hardness <=217 HB Not specified
Condition Annealed, quenched or solution treated bars and flats (Table 3) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 1570 (Part 5) X10Cr17Mn6Ni4
Not documented
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
Can IS 1570 (Part 5) X10Cr17Mn6Ni4 Be Substituted With GOST 5632 12Kh13?
IS 1570 (Part 5) X10Cr17Mn6Ni4 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X10Cr17Mn6Ni4
No active listings currently.
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X10Cr17Mn6Ni4
0 active listings and RFQs →
GOST 5632 12Kh13
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X10Cr17Mn6Ni4 and GOST 5632 12Kh13?
IS 1570 (Part 5) X10Cr17Mn6Ni4 specifies P, S which are not specified for GOST 5632 12Kh13.
Can IS 1570 (Part 5) X10Cr17Mn6Ni4 be substituted with GOST 5632 12Kh13?
IS 1570 (Part 5) X10Cr17Mn6Ni4 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.