IS 1570 (Part 5) X12Cr12 vs GOST 5632 12Kh13

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X12Cr12 (IS 1570 (Part 5):1985) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X12Cr12 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X12Cr12 vs GOST 5632 12Kh13 is a 75.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X12Cr12:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4301 EN 10088-1 1.4845 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
75.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X12Cr12 GOST 5632 12Kh13
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.08-0.15 0.09–0.15
Si (%) <=1.0 ≤0.80
Mn (%) <=1.0 ≤0.80
P (%) <=0.040 Not specified
S (%) <=0.030 Not specified
Cr (%) 11.5-13.5 12.0–14.0
Ni (%) <=1.0 ≤0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X12Cr12 GOST 5632 12Kh13
Tensile Strength >=450 MPa ≥540 MPa (annealed)
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=20.0% (50 mm) Not specified
Hardness <=217 HB; <=95 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 1570 (Part 5) X12Cr12
Not documented
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
Can IS 1570 (Part 5) X12Cr12 Be Substituted With GOST 5632 12Kh13?
IS 1570 (Part 5) X12Cr12 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X12Cr12
No active listings currently.
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X12Cr12
0 active listings and RFQs →
GOST 5632 12Kh13
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X12Cr12 and GOST 5632 12Kh13?
IS 1570 (Part 5) X12Cr12 specifies P, S which are not specified for GOST 5632 12Kh13.
Can IS 1570 (Part 5) X12Cr12 be substituted with GOST 5632 12Kh13?
IS 1570 (Part 5) X12Cr12 and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.