IS 1570 (Part 5) X15Cr16Ni2 vs ASTM A276/A276M S43100

Strong Match — 97% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr16Ni2 (IS 1570 (Part 5):1985) and ASTM A276/A276M S43100 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr16Ni2 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A276/A276M S43100 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X15Cr16Ni2 vs ASTM A276/A276M S43100 is a 95.5% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 97%.

Frequently Compared With IS 1570 (Part 5) X15Cr16Ni2:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4845 ASTM A959 205 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
95.5%
MECHANICAL MATCH
100%
OVERALL
97%
Specifications
Property IS 1570 (Part 5) X15Cr16Ni2 ASTM A276/A276M S43100
Standard IS 1570 (Part 5):1985 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) 0.10-0.20 <=0.20
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 15.0-17.0 15.0-17.0
Ni (%) 1.25-2.50 1.25-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr16Ni2 ASTM A276/A276M S43100
Hardness <=285 HB <=285 HB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Condition A (Annealed), hot-finished or cold-finished, all sizes (first row printed)
Typical Applications
IS 1570 (Part 5) X15Cr16Ni2
Not documented
ASTM A276/A276M S43100
Stainless steel bars and shapes (hot-finished or cold-finished)
Can IS 1570 (Part 5) X15Cr16Ni2 Be Substituted With ASTM A276/A276M S43100?
IS 1570 (Part 5) X15Cr16Ni2 and ASTM A276/A276M S43100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S43100 is often considered as a substitute for IS 1570 (Part 5) X15Cr16Ni2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X15Cr16Ni2
0 active listings and RFQs →
ASTM A276/A276M S43100
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr16Ni2 and ASTM A276/A276M S43100?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X15Cr16Ni2 be substituted with ASTM A276/A276M S43100?
IS 1570 (Part 5) X15Cr16Ni2 and ASTM A276/A276M S43100 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S43100 is often considered as a substitute for IS 1570 (Part 5) X15Cr16Ni2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.