IS 1570 (Part 5) X15Cr16Ni2 vs EN 10088-1 X17CrNi16-2

Strong Match — 92% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr16Ni2 (IS 1570 (Part 5):1985) and EN 10088-1 X17CrNi16-2 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr16Ni2 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X17CrNi16-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X15Cr16Ni2 vs EN 10088-1 X17CrNi16-2 is a 92% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92%.

Frequently Compared With IS 1570 (Part 5) X15Cr16Ni2:
GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4845 ASTM A959 205 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
92%
MECHANICAL MATCH
No shared data
OVERALL
92%
Specifications
Property IS 1570 (Part 5) X15Cr16Ni2 EN 10088-1 X17CrNi16-2
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.10-0.20 0.12-0.22
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.50
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.015
Cr (%) 15.0-17.0 15.0-17.0
Ni (%) 1.25-2.50 1.50-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr16Ni2 EN 10088-1 X17CrNi16-2
Hardness <=285 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Can IS 1570 (Part 5) X15Cr16Ni2 Be Substituted With EN 10088-1 X17CrNi16-2?
IS 1570 (Part 5) X15Cr16Ni2 and EN 10088-1 X17CrNi16-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X17CrNi16-2 is often considered as a substitute for IS 1570 (Part 5) X15Cr16Ni2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X15Cr16Ni2
0 active listings and RFQs →
EN 10088-1 X17CrNi16-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr16Ni2 and EN 10088-1 X17CrNi16-2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X15Cr16Ni2 be substituted with EN 10088-1 X17CrNi16-2?
IS 1570 (Part 5) X15Cr16Ni2 and EN 10088-1 X17CrNi16-2 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X17CrNi16-2 is often considered as a substitute for IS 1570 (Part 5) X15Cr16Ni2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.