IS 1570 (Part 5) X45Cr9Si3 vs EN 10088-1 1.4845

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X45Cr9Si3 (IS 1570 (Part 5):1985) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X45Cr9Si3 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X45Cr9Si3 vs EN 10088-1 1.4845 is a 63.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X45Cr9Si3:
GOST 5632 12Kh13 GOST 5632 08X18H10 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .-
Match Breakdown
CHEMISTRY MATCH
63.6%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X45Cr9Si3 EN 10088-1 1.4845
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.40-0.50 ≤0.10
Si (%) 3.0-3.75 ≤1.50
Mn (%) 0.30-0.60 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.050 Not specified
Cr (%) 7.5-9.5 24.0–26.0
Ni (%) <=0.50 19.0–22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X45Cr9Si3 EN 10088-1 1.4845
Hardness 255-293 HB Not specified
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥515 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Max Service Temp Not specified 1100°C continuous
Typical Applications
IS 1570 (Part 5) X45Cr9Si3
Not documented
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can IS 1570 (Part 5) X45Cr9Si3 Be Substituted With EN 10088-1 1.4845?
IS 1570 (Part 5) X45Cr9Si3 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X45Cr9Si3
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
IS 1570 (Part 5) X45Cr9Si3
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X45Cr9Si3 and EN 10088-1 1.4845?
IS 1570 (Part 5) X45Cr9Si3 specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 1570 (Part 5) X45Cr9Si3 be substituted with EN 10088-1 1.4845?
IS 1570 (Part 5) X45Cr9Si3 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.