IS 1570 (Part 5) X55Cr21Mn8Ni2N vs EN 10088-1 1.4845

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X55Cr21Mn8Ni2N (IS 1570 (Part 5):1985) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X55Cr21Mn8Ni2N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X55Cr21Mn8Ni2N vs EN 10088-1 1.4845 is a 63.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X55Cr21Mn8Ni2N:
GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13 EN 10088-1 1.4301 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
63.1%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X55Cr21Mn8Ni2N EN 10088-1 1.4845
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.50-0.60 ≤0.10
Si (%) <=1.0 ≤1.50
Mn (%) 7.0-9.5 ≤2.00
P (%) <=0.045 Not specified
S (%) <=0.035 Not specified
Cr (%) 20.0-22.0 24.0–26.0
Ni (%) 1.5-2.75 19.0–22.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X55Cr21Mn8Ni2N EN 10088-1 1.4845
Hardness >=321 HB Not specified
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥515 MPa
Yield Strength Not specified ≥205 MPa
Elongation Not specified ≥40%
Max Service Temp Not specified 1100°C continuous
Typical Applications
IS 1570 (Part 5) X55Cr21Mn8Ni2N
Not documented
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
Can IS 1570 (Part 5) X55Cr21Mn8Ni2N Be Substituted With EN 10088-1 1.4845?
IS 1570 (Part 5) X55Cr21Mn8Ni2N and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X55Cr21Mn8Ni2N
No active listings currently.
EN 10088-1 1.4845
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3200 mm (106.3–125.98 in)
On M-EX Right Now
IS 1570 (Part 5) X55Cr21Mn8Ni2N
0 active listings and RFQs →
EN 10088-1 1.4845
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X55Cr21Mn8Ni2N and EN 10088-1 1.4845?
IS 1570 (Part 5) X55Cr21Mn8Ni2N specifies P, S which are not specified for EN 10088-1 1.4845.
Can IS 1570 (Part 5) X55Cr21Mn8Ni2N be substituted with EN 10088-1 1.4845?
IS 1570 (Part 5) X55Cr21Mn8Ni2N and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.