IS 1570 (Part 5) X70Cr21Mn6Ni2N vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X70Cr21Mn6Ni2N (IS 1570 (Part 5):1985) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X70Cr21Mn6Ni2N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X70Cr21Mn6Ni2N vs EN 10088-1 1.4301 is a 62.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X70Cr21Mn6Ni2N:
GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4401 EN 10088-1 1.4845 ASTM A959 .- EN 10088-1 1.4006 GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
62.8%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X70Cr21Mn6Ni2N EN 10088-1 1.4301
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) 0.65-0.75 ≤0.07
Si (%) 0.45-0.85 ≤1.00
Mn (%) 5.5-7.0 ≤2.00
P (%) <=0.045 ≤0.045
S (%) <=0.035 ≤0.030
Cr (%) 20.0-22.0 17.5–19.5
Ni (%) 1.4-1.9 8.0–10.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X70Cr21Mn6Ni2N EN 10088-1 1.4301
Hardness >=321 HB ≤215 HB
Condition Valve steel, hardened and tempered (Table 6) Not specified
Tensile Strength Not specified ≥520 MPa
Yield Strength Not specified ≥210 MPa
Elongation Not specified ≥45%
Typical Applications
IS 1570 (Part 5) X70Cr21Mn6Ni2N
Not documented
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Can IS 1570 (Part 5) X70Cr21Mn6Ni2N Be Substituted With EN 10088-1 1.4301?
IS 1570 (Part 5) X70Cr21Mn6Ni2N and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X70Cr21Mn6Ni2N
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
IS 1570 (Part 5) X70Cr21Mn6Ni2N
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X70Cr21Mn6Ni2N and EN 10088-1 1.4301?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X70Cr21Mn6Ni2N be substituted with EN 10088-1 1.4301?
IS 1570 (Part 5) X70Cr21Mn6Ni2N and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.