IS 1570 (Part 6) 85T6 vs DIN EN ISO 4957 1.2344

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) 85T6 (IS 1570 (Part 6):1996) and DIN EN ISO 4957 1.2344 (DIN EN ISO 4957:2018-11) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) 85T6 is defined under Bureau of Indian Standards (IS), originating from India, while DIN EN ISO 4957 1.2344 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 6) 85T6 vs DIN EN ISO 4957 1.2344 is a 49.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 6) 85T6:
IS 1570 (Part 6) 75T6 IS 1570 (Part 6) 65T6 EN ISO 4957 1.2316 IS 1570 (Part 6) 55T8 IS 1570 (Part 6) 70T6 EN ISO 683-17 100Cr6 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 50T8 IS 1570 (Part 6) 60T6 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 70T3
Match Breakdown
CHEMISTRY MATCH
49.2%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 6) 85T6 DIN EN ISO 4957 1.2344
Standard IS 1570 (Part 6):1996 DIN EN ISO 4957:2018-11
Category Tool & Die Steels Tool & Die Steels
C (%) 0.80-0.90 0.37–0.43
Si (%) 0.10-0.35 0.90–1.20
Mn (%) 0.50-0.80 0.30–0.50
P (%) <=0.035 ≤0.030
S (%) <=0.035 ≤0.030
Cr (%) <=0.20 4.80–5.50
Cu (%) <=0.25 Not specified
Ni (%) <=0.25 Not specified
Mo (%) Not specified 1.20–1.50
V (%) Not specified 0.90–1.10
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) 85T6 DIN EN ISO 4957 1.2344
Hardness (annealed) Not specified ≤229 HB
Hardness (hardened) Not specified 44–52 HRC
Tensile Strength Not specified 1200–1600 MPa
Elongation Not specified ≥8%
Typical Applications
IS 1570 (Part 6) 85T6
Not documented
DIN EN ISO 4957 1.2344
Die casting dies, extrusion dies, forging dies, hot shear blades, mandrels, pressure die casting tooling
Key Differences
Can IS 1570 (Part 6) 85T6 Be Substituted With DIN EN ISO 4957 1.2344?
IS 1570 (Part 6) 85T6 and DIN EN ISO 4957 1.2344 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) 85T6
No active listings currently.
DIN EN ISO 4957 1.2344
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–3700 mm (118.11–145.67 in)
On M-EX Right Now
IS 1570 (Part 6) 85T6
0 active listings and RFQs →
DIN EN ISO 4957 1.2344
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) 85T6 and DIN EN ISO 4957 1.2344?
IS 1570 (Part 6) 85T6 specifies Cu, Ni which are not specified for DIN EN ISO 4957 1.2344. DIN EN ISO 4957 1.2344 specifies Mo, V which are not specified for IS 1570 (Part 6) 85T6.
Can IS 1570 (Part 6) 85T6 be substituted with DIN EN ISO 4957 1.2344?
IS 1570 (Part 6) 85T6 and DIN EN ISO 4957 1.2344 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.