IS 1570 (Part 6) T118Cr2 vs JIS G4404 SKS93

Close Alternative — 76.5% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T118Cr2 (IS 1570 (Part 6):1996) and JIS G4404 SKS93 (JIS G4404:2006) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T118Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while JIS G4404 SKS93 is defined under Japanese Industrial Standards (JIS), originating from Japan.

As per chemical composition, IS 1570 (Part 6) T118Cr2 vs JIS G4404 SKS93 is a 76.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.5%.

Frequently Compared With IS 1570 (Part 6) T118Cr2:
EN ISO 683-17 100Cr6 GOST 5950 3H2W8F EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 133T3 DIN EN ISO 4957 1.2344 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 GB/T 1299 3Cr2W8V AISI 52100
Match Breakdown
CHEMISTRY MATCH
76.5%
MECHANICAL MATCH
No shared data
OVERALL
76.5%
Specifications
Property IS 1570 (Part 6) T118Cr2 JIS G4404 SKS93
Standard IS 1570 (Part 6):1996 JIS G4404:2006
Category Tool & Die Steels Tool & Die Steels
C (%) 1.10-1.25 1.00-1.10
Si (%) 0.10-0.35 <=0.50
Mn (%) <=0.40 0.80-1.10
Cr (%) 0.30-0.60 0.20-0.60
V (%) <=0.30 Not specified
P (%) <=0.035 <=0.03
S (%) <=0.035 <=0.03
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T118Cr2 JIS G4404 SKS93
Hardness HRC (hardened) Not specified 60–64
Hardness HB (annealed) Not specified ≤212
Typical Applications
IS 1570 (Part 6) T118Cr2
Not documented
JIS G4404 SKS93
Cold working molds, press dies, blanking dies, shear blades, gauges, jigs.
Key Differences
Can IS 1570 (Part 6) T118Cr2 Be Substituted With JIS G4404 SKS93?
IS 1570 (Part 6) T118Cr2 and JIS G4404 SKS93 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) T118Cr2
No active listings currently.
JIS G4404 SKS93
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3200–3300 mm (125.98–129.92 in)
On M-EX Right Now
IS 1570 (Part 6) T118Cr2
0 active listings and RFQs →
JIS G4404 SKS93
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T118Cr2 and JIS G4404 SKS93?
IS 1570 (Part 6) T118Cr2 specifies V which is not specified for JIS G4404 SKS93.
Can IS 1570 (Part 6) T118Cr2 be substituted with JIS G4404 SKS93?
IS 1570 (Part 6) T118Cr2 and JIS G4404 SKS93 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.