IS 1570 (Part 6) T135Cr2 vs IS 3748 T118Cr2

Strong Match — 90.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T135Cr2 (IS 1570 (Part 6):1996) and IS 3748 T118Cr2 (IS 3748:1990) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T135Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 3748 T118Cr2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 6) T135Cr2 vs IS 3748 T118Cr2 is a 90.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 90.8%.

Frequently Compared With IS 1570 (Part 6) T135Cr2:
EN ISO 683-17 100Cr6 EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 133T3 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV1 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 GB/T 1299 3Cr2W8V AISI 52100
Match Breakdown
CHEMISTRY MATCH
90.8%
MECHANICAL MATCH
No shared data
OVERALL
90.8%
Specifications
Property IS 1570 (Part 6) T135Cr2 IS 3748 T118Cr2
Standard IS 1570 (Part 6):1996 IS 3748:1990
Category Tool & Die Steels Tool & Die Steels
C (%) 1.25-1.40 1.10-1.25
Si (%) 0.10-0.35 0.10-0.30
Mn (%) <=0.40 <=0.40
Cr (%) 0.30-0.60 0.30-0.60
V (%) <=0.30 <=0.30
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T135Cr2 IS 3748 T118Cr2
Hardness Not specified <=220 HB
Condition Not specified Annealed (maximum Brinell hardness)
Typical Applications
IS 1570 (Part 6) T135Cr2
Not documented
IS 3748 T118Cr2
Cold work tools and dies for blanking, trimming, chipping and shearing
Can IS 1570 (Part 6) T135Cr2 Be Substituted With IS 3748 T118Cr2?
IS 1570 (Part 6) T135Cr2 and IS 3748 T118Cr2 overlap closely enough on chemistry and mechanical properties that IS 3748 T118Cr2 is often considered as a substitute for IS 1570 (Part 6) T135Cr2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 6) T135Cr2
0 active listings and RFQs →
IS 3748 T118Cr2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T135Cr2 and IS 3748 T118Cr2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) T135Cr2 be substituted with IS 3748 T118Cr2?
IS 1570 (Part 6) T135Cr2 and IS 3748 T118Cr2 overlap closely enough on chemistry and mechanical properties that IS 3748 T118Cr2 is often considered as a substitute for IS 1570 (Part 6) T135Cr2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.