IS 1570 (Part 6) T30Ni16Cr5 vs IS 3748 T30Ni16Cr5

Strong Match — 98.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T30Ni16Cr5 (IS 1570 (Part 6):1996) and IS 3748 T30Ni16Cr5 (IS 3748:1990) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T30Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 3748 T30Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 6) T30Ni16Cr5 vs IS 3748 T30Ni16Cr5 is a 98.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.4%.

Frequently Compared With IS 1570 (Part 6) T30Ni16Cr5:
EN ISO 4957 1.2316 GB/T 1299 3Cr2W8V GOST 5950 3H2W8F EN ISO 683-17 100Cr6 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS1 IS 1570 (Part 6) 103T3 DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3
Match Breakdown
CHEMISTRY MATCH
98.4%
MECHANICAL MATCH
No shared data
OVERALL
98.4%
Specifications
Property IS 1570 (Part 6) T30Ni16Cr5 IS 3748 T30Ni16Cr5
Standard IS 1570 (Part 6):1996 IS 3748:1990
Category Tool & Die Steels Tool & Die Steels
C (%) 0.25-0.35 0.26-0.34
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 3.90-4.30 3.90-4.30
Cr (%) 1.10-1.40 1.10-1.40
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T30Ni16Cr5 IS 3748 T30Ni16Cr5
Hardness Not specified <=255 HB
Condition Not specified Annealed (maximum Brinell hardness)
Typical Applications
IS 1570 (Part 6) T30Ni16Cr5
Not documented
IS 3748 T30Ni16Cr5
Cold work tools and dies for blanking, trimming, chipping and shearing
Can IS 1570 (Part 6) T30Ni16Cr5 Be Substituted With IS 3748 T30Ni16Cr5?
IS 1570 (Part 6) T30Ni16Cr5 and IS 3748 T30Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 3748 T30Ni16Cr5 is often considered as a substitute for IS 1570 (Part 6) T30Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 6) T30Ni16Cr5
0 active listings and RFQs →
IS 3748 T30Ni16Cr5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T30Ni16Cr5 and IS 3748 T30Ni16Cr5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) T30Ni16Cr5 be substituted with IS 3748 T30Ni16Cr5?
IS 1570 (Part 6) T30Ni16Cr5 and IS 3748 T30Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 3748 T30Ni16Cr5 is often considered as a substitute for IS 1570 (Part 6) T30Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.