IS 1570 (Part 6) T40Ni6Cr4Mo3 vs ASTM A681 P2

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T40Ni6Cr4Mo3 (IS 1570 (Part 6):1996) and ASTM A681 P2 (ASTM A681:2008) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T40Ni6Cr4Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A681 P2 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 6) T40Ni6Cr4Mo3 vs ASTM A681 P2 is a 70.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 6) T40Ni6Cr4Mo3:
GB/T 1299 3Cr2W8V GB/T 1299 4Cr5MoSiV1 EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 EN ISO 683-17 100Cr6 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 133T3 GOST 5950 4H5MFS1 GOST 5950 4H5MFS IS 1570 (Part 6) 118T3
Match Breakdown
CHEMISTRY MATCH
70.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 6) T40Ni6Cr4Mo3 ASTM A681 P2
Standard IS 1570 (Part 6):1996 ASTM A681:2008
Category Tool & Die Steels Tool & Die Steels
C (%) 0.35-0.45 <=0.10
Si (%) 0.10-0.35 0.10-0.40
Mn (%) 0.40-0.70 0.10-0.40
Ni (%) 1.25-1.75 0.10-0.50
Cr (%) 0.90-1.30 0.75-1.25
Mo (%) 0.20-0.35 0.15-0.40
P (%) <=0.035 <=0.030
S (%) <=0.035 <=0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T40Ni6Cr4Mo3 ASTM A681 P2
Hardness Not specified <=100 HB
Condition Not specified Annealed (maximum Brinell hardness)
Typical Applications
IS 1570 (Part 6) T40Ni6Cr4Mo3
Not documented
ASTM A681 P2
Injection mould cavities, die casting dies for zinc
Can IS 1570 (Part 6) T40Ni6Cr4Mo3 Be Substituted With ASTM A681 P2?
IS 1570 (Part 6) T40Ni6Cr4Mo3 and ASTM A681 P2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) T40Ni6Cr4Mo3
No active listings currently.
ASTM A681 P2
Round Bar → (3 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2700–3900 mm (106.3–153.54 in)
On M-EX Right Now
IS 1570 (Part 6) T40Ni6Cr4Mo3
0 active listings and RFQs →
ASTM A681 P2
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T40Ni6Cr4Mo3 and ASTM A681 P2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) T40Ni6Cr4Mo3 be substituted with ASTM A681 P2?
IS 1570 (Part 6) T40Ni6Cr4Mo3 and ASTM A681 P2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.