Post Stock Login Register

IS 1570 (Part 6) T40W8Cr5V2 vs GOST 5950 3H2W8F

Related Material — 60.5% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T40W8Cr5V2 (IS 1570 (Part 6):1996) and GOST 5950 3H2W8F (GOST 5950-2000) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) T40W8Cr5V2 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 6) T40W8Cr5V2 vs GOST 5950 3H2W8F is a 60.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 60.5%.

Frequently Compared With IS 1570 (Part 6) T40W8Cr5V2:
GB/T 1299 3Cr2W8V EN ISO 683-17 100Cr6 GOST 5950 4H5MFS EN ISO 4957 1.2316 IS 1570 (Part 6) 103T3 GOST 5950 4H5MFS1 GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 DIN EN ISO 4957 1.2344
Match Breakdown
CHEMISTRY MATCH
60.5%
MECHANICAL MATCH
No shared data
OVERALL
60.5%
Specifications
Property IS 1570 (Part 6) T40W8Cr5V2 GOST 5950 3H2W8F
Standard IS 1570 (Part 6):1996 GOST 5950-2000
Category Tool & Die Steels Tool & Die Steels
C (%) 0.35-0.45 0.3-0.4
Si (%) 0.50-1.00 0.2-0.5
Mn (%) 0.20-0.40 Not specified
Cr (%) 1.00-1.50 2.2-2.7
V (%) 0.10-0.25 0.3-0.6
W (%) 1.75-2.25 7.5-9.0
P (%) <=0.035 Not specified
S (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T40W8Cr5V2 GOST 5950 3H2W8F
Tensile Strength Not specified 1400-1700 MPa
Yield Strength Not specified 1200 MPa min
Elongation Not specified 8% min
Hardness Not specified 45-50 HRC
Typical Applications
IS 1570 (Part 6) T40W8Cr5V2
Not documented
GOST 5950 3H2W8F
Used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.
Key Differences
Can IS 1570 (Part 6) T40W8Cr5V2 Be Substituted With GOST 5950 3H2W8F?
IS 1570 (Part 6) T40W8Cr5V2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) T40W8Cr5V2
No active listings currently.
GOST 5950 3H2W8F
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–4300 mm (110.24–169.29 in)
On M-EX Right Now
IS 1570 (Part 6) T40W8Cr5V2
0 active listings and RFQs →
GOST 5950 3H2W8F
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T40W8Cr5V2 and GOST 5950 3H2W8F?
IS 1570 (Part 6) T40W8Cr5V2 specifies Mn, P, S which are not specified for GOST 5950 3H2W8F.
Can IS 1570 (Part 6) T40W8Cr5V2 be substituted with GOST 5950 3H2W8F?
IS 1570 (Part 6) T40W8Cr5V2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.