IS 1570 (Part 6) T55Ni7Cr4Mo5V1 vs IS 4432 15Ni7Cr4Mo2

Related Material — 65% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) T55Ni7Cr4Mo5V1 (IS 1570 (Part 6):1996) and IS 4432 15Ni7Cr4Mo2 (IS 4432:1988) are both steel grades. IS 1570 (Part 6) T55Ni7Cr4Mo5V1 is classified under Tool & Die Steels, while IS 4432 15Ni7Cr4Mo2 is classified under Alloy Steel — a different category, which is worth noting alongside the chemistry match below. IS 1570 (Part 6) T55Ni7Cr4Mo5V1 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4432 15Ni7Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 6) T55Ni7Cr4Mo5V1 vs IS 4432 15Ni7Cr4Mo2 is a 67.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65%.

Frequently Compared With IS 1570 (Part 6) T55Ni7Cr4Mo5V1:
IS 1570 (Part 6) 103T3 GB/T 1299 4Cr5MoSiV1 DIN EN ISO 4957 1.2344 GOST 5950 3H2W8F GOST 5950 4H5MFS EN ISO 683-17 100Cr6 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 118T3 GB/T 1299 3Cr2W8V
Match Breakdown
CHEMISTRY MATCH
67.8%
MECHANICAL MATCH
No shared data
OVERALL
65%
Specifications
Property IS 1570 (Part 6) T55Ni7Cr4Mo5V1 IS 4432 15Ni7Cr4Mo2
Standard IS 1570 (Part 6):1996 IS 4432:1988
Category Tool & Die Steels Alloy Steel
C (%) 0.50-0.60 0.12-0.18
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.65-0.95 0.60-1.00
Ni (%) 1.50-1.80 1.50-2.00
Cr (%) 1.00-1.20 0.75-1.25
Mo (%) 0.45-0.55 0.10-0.20
V (%) 0.07-0.12 Not specified
P (%) <=0.035 <=0.035
S (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) T55Ni7Cr4Mo5V1 IS 4432 15Ni7Cr4Mo2
Core Tensile Strength Not specified 1100-1400 MPa (16 mm) / 1050-1400 MPa (30 mm) / 800-1100 MPa (63 mm)
Core Yield Strength Not specified >=750 MPa (16 mm) / >=730 MPa (30 mm) / >=550 MPa (63 mm)
Core Elongation Not specified >=9% (16 mm) / >=10% (30 mm) / >=12% (63 mm)
Core Reduction of Area Not specified >=40% (16 mm) / >=40% (30 mm) / >=45% (63 mm)
Hardness, annealed (A) Not specified <=229 HB
Typical Applications
IS 1570 (Part 6) T55Ni7Cr4Mo5V1
Not documented
IS 4432 15Ni7Cr4Mo2
Forgings and fabrication of case-hardened machine or automobile parts
Key Differences
Can IS 1570 (Part 6) T55Ni7Cr4Mo5V1 Be Substituted With IS 4432 15Ni7Cr4Mo2?
IS 1570 (Part 6) T55Ni7Cr4Mo5V1 and IS 4432 15Ni7Cr4Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 6) T55Ni7Cr4Mo5V1
0 active listings and RFQs →
IS 4432 15Ni7Cr4Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) T55Ni7Cr4Mo5V1 and IS 4432 15Ni7Cr4Mo2?
Different category: IS 1570 (Part 6) T55Ni7Cr4Mo5V1 is Tool & Die Steels, IS 4432 15Ni7Cr4Mo2 is Alloy Steel. IS 1570 (Part 6) T55Ni7Cr4Mo5V1 specifies V which is not specified for IS 4432 15Ni7Cr4Mo2.
Can IS 1570 (Part 6) T55Ni7Cr4Mo5V1 be substituted with IS 4432 15Ni7Cr4Mo2?
IS 1570 (Part 6) T55Ni7Cr4Mo5V1 and IS 4432 15Ni7Cr4Mo2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.