IS 1570 (Part 6) XT100Mo9Cr4W2V2 vs GOST 5950 3H2W8F

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT100Mo9Cr4W2V2 (IS 1570 (Part 6):1996) and GOST 5950 3H2W8F (GOST 5950-2000) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT100Mo9Cr4W2V2 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 6) XT100Mo9Cr4W2V2 vs GOST 5950 3H2W8F is a 45.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 6) XT100Mo9Cr4W2V2:
GOST 5950 4H5MFS1 EN ISO 4957 1.2316 EN ISO 683-17 100Cr6 GOST 5950 4H5MFS GB/T 1299 3Cr2W8V DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 GB/T 1299 4Cr5MoSiV1 GB/T 1299 4Cr5MoSiV
Match Breakdown
CHEMISTRY MATCH
45.4%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 1570 (Part 6) XT100Mo9Cr4W2V2 GOST 5950 3H2W8F
Standard IS 1570 (Part 6):1996 GOST 5950-2000
Category Tool & Die Steels Tool & Die Steels
C (%) 0.95-1.05 0.3-0.4
Cr (%) 3.50-4.50 2.2-2.7
Mo (%) 8.00-9.00 Not specified
V (%) 1.70-2.20 0.3-0.6
W (%) 1.50-2.10 7.5-9.0
Co (%) <=1.00 Not specified
Si (%) <=0.50 0.2-0.5
Mn (%) <=0.40 Not specified
P (%) <=0.030 Not specified
S (%) <=0.030 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT100Mo9Cr4W2V2 GOST 5950 3H2W8F
Tensile Strength Not specified 1400-1700 MPa
Yield Strength Not specified 1200 MPa min
Elongation Not specified 8% min
Hardness Not specified 45-50 HRC
Typical Applications
IS 1570 (Part 6) XT100Mo9Cr4W2V2
Not documented
GOST 5950 3H2W8F
Used for forging dies, extrusion tools, hot punches, mandrels, and die inserts.
Key Differences
Can IS 1570 (Part 6) XT100Mo9Cr4W2V2 Be Substituted With GOST 5950 3H2W8F?
IS 1570 (Part 6) XT100Mo9Cr4W2V2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) XT100Mo9Cr4W2V2
No active listings currently.
GOST 5950 3H2W8F
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–4300 mm (110.24–169.29 in)
On M-EX Right Now
IS 1570 (Part 6) XT100Mo9Cr4W2V2
0 active listings and RFQs →
GOST 5950 3H2W8F
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT100Mo9Cr4W2V2 and GOST 5950 3H2W8F?
IS 1570 (Part 6) XT100Mo9Cr4W2V2 specifies Mo, Co, Mn, P which are not specified for GOST 5950 3H2W8F.
Can IS 1570 (Part 6) XT100Mo9Cr4W2V2 be substituted with GOST 5950 3H2W8F?
IS 1570 (Part 6) XT100Mo9Cr4W2V2 and GOST 5950 3H2W8F share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.