IS 1570 (Part 6) XT215Cr12 vs EN ISO 683-17 100Cr6

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT215Cr12 (IS 1570 (Part 6):1996) and EN ISO 683-17 100Cr6 (EN ISO 683-17:2014) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT215Cr12 is defined under Bureau of Indian Standards (IS), originating from India, while EN ISO 683-17 100Cr6 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 6) XT215Cr12 vs EN ISO 683-17 100Cr6 is a 80% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 6) XT215Cr12:
DIN EN ISO 4957 1.2344 GB/T 1299 4Cr5MoSiV1 EN ISO 4957 1.2316 GB/T 1299 4Cr5MoSiV AISI 52100 GB/T 1299 3Cr2W8V GOST 5950 3H2W8F DIN EN ISO 4957 1.2379 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 IS 3748 103T3
Match Breakdown
CHEMISTRY MATCH
80%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 6) XT215Cr12 EN ISO 683-17 100Cr6
Standard IS 1570 (Part 6):1996 EN ISO 683-17:2014
Category Tool & Die Steels Tool & Die Steels
C (%) 2.00-2.30 0.93–1.05
Si (%) 0.10-0.35 0.15–0.35
Mn (%) 0.25-0.50 0.25–0.45
Cr (%) 11.0-13.0 1.35–1.65
Mo (%) <=0.80 (optional) Not specified
V (%) <=0.80 (optional) Not specified
P (%) <=0.035 ≤0.025
S (%) <=0.035 ≤0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT215Cr12 EN ISO 683-17 100Cr6
Tensile Strength Not specified ≥620 MPa (annealed)
Hardness HRC Not specified 60–66 (hardened)
Hardness HB Not specified 179–217 (annealed)
Typical Applications
IS 1570 (Part 6) XT215Cr12
Not documented
EN ISO 683-17 100Cr6
Rolling element bearings, precision components, cold work tooling
Key Differences
Can IS 1570 (Part 6) XT215Cr12 Be Substituted With EN ISO 683-17 100Cr6?
IS 1570 (Part 6) XT215Cr12 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) XT215Cr12
No active listings currently.
EN ISO 683-17 100Cr6
Round Bar → (18 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–6500 mm (118.11–255.91 in)
On M-EX Right Now
IS 1570 (Part 6) XT215Cr12
0 active listings and RFQs →
EN ISO 683-17 100Cr6
18 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT215Cr12 and EN ISO 683-17 100Cr6?
IS 1570 (Part 6) XT215Cr12 specifies Mo, V which are not specified for EN ISO 683-17 100Cr6.
Can IS 1570 (Part 6) XT215Cr12 be substituted with EN ISO 683-17 100Cr6?
IS 1570 (Part 6) XT215Cr12 and EN ISO 683-17 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.