IS 1570 (Part 6) XT33W9Cr3V4 vs GB/T 1299 3Cr2W8V

Close Alternative — 78.1% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 6) XT33W9Cr3V4 (IS 1570 (Part 6):1996) and GB/T 1299 3Cr2W8V (GB/T 1299-2014) are both steel grades. Both fall under the Tool & Die Steels category. IS 1570 (Part 6) XT33W9Cr3V4 is defined under Bureau of Indian Standards (IS), originating from India, while GB/T 1299 3Cr2W8V is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, IS 1570 (Part 6) XT33W9Cr3V4 vs GB/T 1299 3Cr2W8V is a 78.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 78.1%.

Frequently Compared With IS 1570 (Part 6) XT33W9Cr3V4:
GOST 5950 3H2W8F GOST 5950 4H5MFS1 EN ISO 4957 1.2316 GOST 5950 4H5MFS EN ISO 683-17 100Cr6 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 GB/T 1299 4Cr5MoSiV1 DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 GB/T 1299 4Cr5MoSiV IS 1570 (Part 6) 133T3
Match Breakdown
CHEMISTRY MATCH
78.1%
MECHANICAL MATCH
No shared data
OVERALL
78.1%
Specifications
Property IS 1570 (Part 6) XT33W9Cr3V4 GB/T 1299 3Cr2W8V
Standard IS 1570 (Part 6):1996 GB/T 1299-2014
Category Tool & Die Steels Tool & Die Steels
C (%) 0.25-0.40 0.30-0.40
Si (%) 0.10-0.35 0.20-0.40
Mn (%) 0.20-0.40 0.20-0.50
Cr (%) 2.80-3.30 2.20-2.70
V (%) 0.25-0.50 0.20-0.50
W (%) 8.0-10.0 7.50-9.00
P (%) <=0.035 0.030 max
S (%) <=0.035 0.030 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 6) XT33W9Cr3V4 GB/T 1299 3Cr2W8V
Tensile Strength Not specified 1180-1380 MPa
Yield Strength Not specified 980-1180 MPa
Elongation Not specified 10-14%
Hardness Not specified 48-54 HRC
Typical Applications
IS 1570 (Part 6) XT33W9Cr3V4
Not documented
GB/T 1299 3Cr2W8V
Used for hot forging dies, extrusion dies, die-casting molds, hot punches, and hot shear blades.
Can IS 1570 (Part 6) XT33W9Cr3V4 Be Substituted With GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) XT33W9Cr3V4 and GB/T 1299 3Cr2W8V are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
IS 1570 (Part 6) XT33W9Cr3V4
No active listings currently.
GB/T 1299 3Cr2W8V
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–2900 mm (110.24–114.17 in)
On M-EX Right Now
IS 1570 (Part 6) XT33W9Cr3V4
0 active listings and RFQs →
GB/T 1299 3Cr2W8V
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 6) XT33W9Cr3V4 and GB/T 1299 3Cr2W8V?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 6) XT33W9Cr3V4 be substituted with GB/T 1299 3Cr2W8V?
IS 1570 (Part 6) XT33W9Cr3V4 and GB/T 1299 3Cr2W8V are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.