Related Material — 67.2% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 7) 10Mo6H (IS 1570 (Part 7):1992) and SAE J404 4130 (SAE J404:2009) are both steel grades.
Both fall under the Alloy Steel category.
IS 1570 (Part 7) 10Mo6H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while SAE J404 4130 is commonly used for aircraft structures, pressure vessels, high tensile tubes.
IS 1570 (Part 7) 10Mo6H is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 4130 is defined under SAE International, originating from United States.
As per chemical composition, IS 1570 (Part 7) 10Mo6H vs SAE J404 4130 is a 67.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 67.2%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 7) 10Mo6H
SAE J404 4130
Tensile Strength
>=415 MPa
Not specified
Yield Strength
>=205 MPa (0.2 % proof stress)
Not specified
Elongation
>=30%
Not specified
Condition
Tubes, N+T, thickness - (first row of Table 3)
Not specified
Typical Applications
IS 1570 (Part 7) 10Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
SAE J404 4130
Aircraft structures, pressure vessels, high tensile tubes
Can IS 1570 (Part 7) 10Mo6H Be Substituted With SAE J404 4130?
IS 1570 (Part 7) 10Mo6H and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 1570 (Part 7) 10Mo6H and SAE J404 4130?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) 10Mo6H be substituted with SAE J404 4130?
IS 1570 (Part 7) 10Mo6H and SAE J404 4130 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.