Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 7) 10Mo6H (IS 1570 (Part 7):1992) and BS 970 (Part 3) 722M24 (BS 970 (Part 3):1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 1570 (Part 7) 10Mo6H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while BS 970 (Part 3) 722M24 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (table 16).
IS 1570 (Part 7) 10Mo6H is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 722M24 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, IS 1570 (Part 7) 10Mo6H vs BS 970 (Part 3) 722M24 is a 70.3% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a related material overall at 69.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 7) 10Mo6H
BS 970 (Part 3) 722M24
Tensile Strength
>=415 MPa
Not specified
Yield Strength
>=205 MPa (0.2 % proof stress)
Not specified
Elongation
>=30%
Not specified
Condition
Tubes, N+T, thickness - (first row of Table 3)
Not specified
Typical Applications
IS 1570 (Part 7) 10Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
BS 970 (Part 3) 722M24
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; alloy direct hardening steel (Table 16)
Can IS 1570 (Part 7) 10Mo6H Be Substituted With BS 970 (Part 3) 722M24?
IS 1570 (Part 7) 10Mo6H and BS 970 (Part 3) 722M24 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 1570 (Part 7) 10Mo6H and BS 970 (Part 3) 722M24?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) 10Mo6H be substituted with BS 970 (Part 3) 722M24?
IS 1570 (Part 7) 10Mo6H and BS 970 (Part 3) 722M24 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.