Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 7) 15Mo6H (IS 1570 (Part 7):1992) and NF A35-565 100C6 are both steel grades.
Both fall under the Alloy Steel category.
IS 1570 (Part 7) 15Mo6H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while NF A35-565 100C6 is commonly used for ball bearings, roller bearings, bearing races, rollers, precision tools, wear resistant parts.
IS 1570 (Part 7) 15Mo6H is defined under Bureau of Indian Standards (IS), originating from India, while NF A35-565 100C6 is defined under Association Francaise de Normalisation (NF), originating from France.
As per chemical composition, IS 1570 (Part 7) 15Mo6H vs NF A35-565 100C6 is a 64.9% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 7) 15Mo6H
NF A35-565 100C6
Tensile Strength
>=380 MPa
850-1100 MPa
Yield Strength
>=205 MPa (0.2 % proof stress)
Not specified
Elongation
>=22%
Not specified
Condition
Tubes, N+T, thickness - (first row of Table 3)
Not specified
Hardness
Not specified
60-66 HRC
Typical Applications
IS 1570 (Part 7) 15Mo6H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 7) 15Mo6H specifies Mo which is not specified for NF A35-565 100C6.
NF A35-565 100C6 specifies Cr which is not specified for IS 1570 (Part 7) 15Mo6H.
Can IS 1570 (Part 7) 15Mo6H Be Substituted With NF A35-565 100C6?
IS 1570 (Part 7) 15Mo6H and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 1570 (Part 7) 15Mo6H and NF A35-565 100C6?
IS 1570 (Part 7) 15Mo6H specifies Mo which is not specified for NF A35-565 100C6. NF A35-565 100C6 specifies Cr which is not specified for IS 1570 (Part 7) 15Mo6H.
Can IS 1570 (Part 7) 15Mo6H be substituted with NF A35-565 100C6?
IS 1570 (Part 7) 15Mo6H and NF A35-565 100C6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.