Minimal Match — 32.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 20Cr12MoNiVH (IS 1570 (Part 7):1992) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 20Cr12MoNiVH is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. IS 1570 (Part 7) 20Cr12MoNiVH is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 7) 20Cr12MoNiVH vs GOST 5632 08X18H10 is a 49.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.8%.

Frequently Compared With IS 1570 (Part 7) 20Cr12MoNiVH:
IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 EN 10088-1 1.4301 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28
Match Breakdown
CHEMISTRY MATCH
49.2%
MECHANICAL MATCH
0%
OVERALL
32.8%
Specifications
Property IS 1570 (Part 7) 20Cr12MoNiVH GOST 5632 08X18H10
Standard IS 1570 (Part 7):1992 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) 0.17-0.23 ≤0.08
Si (%) <=0.50 ≤0.80
Mn (%) <=1.00 ≤2.00
P (%) <=0.040 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 11.0-12.50 17.0–19.0
Ni (%) 0.30-1.00 9.0–11.0
Mo (%) 0.7-1.20 Not specified
V (%) 0.20-0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 20Cr12MoNiVH GOST 5632 08X18H10
Tensile Strength 780-930 MPa ≥520 MPa
Yield Strength >=590 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=14% ≥40%
Condition Bars, forgings, Q+T1, thickness up to 250 (first row of Table 3) Not specified
Typical Applications
IS 1570 (Part 7) 20Cr12MoNiVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 7) 20Cr12MoNiVH Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 7) 20Cr12MoNiVH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 20Cr12MoNiVH
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 7) 20Cr12MoNiVH
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 20Cr12MoNiVH and GOST 5632 08X18H10?
IS 1570 (Part 7) 20Cr12MoNiVH specifies Mo, V which are not specified for GOST 5632 08X18H10.
Can IS 1570 (Part 7) 20Cr12MoNiVH be substituted with GOST 5632 08X18H10?
IS 1570 (Part 7) 20Cr12MoNiVH and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.