IS 1570 (Part 7) 3Cr17Ni12Mo3H vs IS 1570 (Part 7) 12Cr12Ni2Mo

Minimal Match — 32.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 3Cr17Ni12Mo3H (IS 1570 (Part 7):1992) and IS 1570 (Part 7) 12Cr12Ni2Mo (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 3Cr17Ni12Mo3H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while IS 1570 (Part 7) 12Cr12Ni2Mo is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. IS 1570 (Part 7) 3Cr17Ni12Mo3H is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr12Ni2Mo is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 7) 3Cr17Ni12Mo3H vs IS 1570 (Part 7) 12Cr12Ni2Mo is a 49.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 32.9%.

Frequently Compared With IS 1570 (Part 7) 3Cr17Ni12Mo3H:
ASTM A959 29-4C ASTM A959 26-3-3 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
49.4%
MECHANICAL MATCH
0%
OVERALL
32.9%
Specifications
Property IS 1570 (Part 7) 3Cr17Ni12Mo3H IS 1570 (Part 7) 12Cr12Ni2Mo
Standard IS 1570 (Part 7):1992 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08-0.16
Si (%) <=1.00 <=0.35
Mn (%) <=2.00 0.50-0.90
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 16.00-18.00 11.0-12.5
Ni (%) 10.00-14.00 2.0-3.0
Mo (%) 2.00-3.00 1.5-2.00
V (%) Not specified 0.25-0.40
N (%) Not specified 0.02-0.04
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 3Cr17Ni12Mo3H IS 1570 (Part 7) 12Cr12Ni2Mo
Tensile Strength 490-690 MPa 930-1130 MPa
Yield Strength >=185 MPa (0.2 % proof stress) >=785 MPa (0.2 % proof stress)
Elongation >=30% >=14%
Condition Tubes, plates, Q, thickness - (first row of Table 3) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
IS 1570 (Part 7) 3Cr17Ni12Mo3H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
IS 1570 (Part 7) 12Cr12Ni2Mo
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 1570 (Part 7) 3Cr17Ni12Mo3H Be Substituted With IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 3Cr17Ni12Mo3H and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 7) 3Cr17Ni12Mo3H
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12Ni2Mo
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 3Cr17Ni12Mo3H and IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 12Cr12Ni2Mo specifies V, N which are not specified for IS 1570 (Part 7) 3Cr17Ni12Mo3H.
Can IS 1570 (Part 7) 3Cr17Ni12Mo3H be substituted with IS 1570 (Part 7) 12Cr12Ni2Mo?
IS 1570 (Part 7) 3Cr17Ni12Mo3H and IS 1570 (Part 7) 12Cr12Ni2Mo share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.