IS 1570 (Part 7) 6Cr17Ni12Mo2H vs EN 10088-1 1.4006

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 7) 6Cr17Ni12Mo2H (IS 1570 (Part 7):1992) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 7) 6Cr17Ni12Mo2H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while EN 10088-1 1.4006 is commonly used for cutlery, turbine blades, fasteners, surgical instruments. IS 1570 (Part 7) 6Cr17Ni12Mo2H is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 7) 6Cr17Ni12Mo2H vs EN 10088-1 1.4006 is a 54.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 7) 6Cr17Ni12Mo2H:
GOST 5632 12Kh13 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
54.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 7) 6Cr17Ni12Mo2H EN 10088-1 1.4006
Standard IS 1570 (Part 7):1992 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 0.08–0.15
Si (%) <=1.00 ≤1.00
Mn (%) <=2.00 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 16.00-18.00 11.5–13.5
Ni (%) 10.00-14.00 ≤0.75
Mo (%) 2.00-3.00 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 7) 6Cr17Ni12Mo2H EN 10088-1 1.4006
Tensile Strength 510-710 MPa ≥540 MPa (annealed)
Yield Strength >=205 MPa (0.2 % proof stress) Not specified
Elongation >=30% ≥18%
Condition Pipes, bars, forgings, plates, Q, thickness - (first row of Table 3) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 1570 (Part 7) 6Cr17Ni12Mo2H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 1570 (Part 7) 6Cr17Ni12Mo2H Be Substituted With EN 10088-1 1.4006?
IS 1570 (Part 7) 6Cr17Ni12Mo2H and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 7) 6Cr17Ni12Mo2H
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 1570 (Part 7) 6Cr17Ni12Mo2H
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 7) 6Cr17Ni12Mo2H and EN 10088-1 1.4006?
IS 1570 (Part 7) 6Cr17Ni12Mo2H specifies P, S, Mo which are not specified for EN 10088-1 1.4006.
Can IS 1570 (Part 7) 6Cr17Ni12Mo2H be substituted with EN 10088-1 1.4006?
IS 1570 (Part 7) 6Cr17Ni12Mo2H and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.