Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 7) 7Cr18Ni10H (IS 1570 (Part 7):1992) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 1570 (Part 7) 7Cr18Ni10H is typically used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 1570 (Part 7) 7Cr18Ni10H is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 1570 (Part 7) 7Cr18Ni10H vs GOST 5632 08X18H10 is a 73.6% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 1570 (Part 7) 7Cr18Ni10H:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 7) 7Cr18Ni10H
GOST 5632 08X18H10
Tensile Strength
490-690 MPa
≥520 MPa
Yield Strength
>=195 MPa (0.2 % proof stress)
≥205 MPa
Elongation
>=30%
≥40%
Condition
Tubes, forgings, plates, Q, thickness - (first row of Table 3)
Not specified
Typical Applications
IS 1570 (Part 7) 7Cr18Ni10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Can IS 1570 (Part 7) 7Cr18Ni10H Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 7) 7Cr18Ni10H and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 1570 (Part 7) 7Cr18Ni10H and GOST 5632 08X18H10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 7) 7Cr18Ni10H be substituted with GOST 5632 08X18H10?
IS 1570 (Part 7) 7Cr18Ni10H and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.