IS 2062 (Part 1):2025 E235BR Steel: Specifications & Listings

IS 2062 (Part 1):2025 E235BR: E235BR is grade E 235, quality BR, in IS 2062 (Part 1):2025 (Structural Steel, Part 1: Hot Rolled Medium and High Tensile Steel), which covers plates, sheets, strips, shapes, sections, flats, bars and rods for structural work. The grade is named by its minimum yield stress.

Category: Structural Steel
Grade Details
GradeIS 2062 (Part 1):2025 E235BR
Standard IS 2062 (Part 1):2025
ApplicationsStructural work: welded, bolted and riveted structures and general engineering purposes
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
IS 2062 (Part 1) E235A IS 2062 (Part 1):2025 Strong Match
IS 2062 (Part 1) E235B0 IS 2062 (Part 1):2025 Strong Match
IS 2062 (Part 1) E235C IS 2062 (Part 1):2025 Strong Match
AS/NZS 3678 Grade 450 AS/NZS 3678:2016 Strong Match
AS/NZS Grade 500 AS/NZS 3597:2008 Strong Match
IS 2062 (Part 1) E250C IS 2062 (Part 1):2025 Strong Match
IS 2062 (Part 1) E275C IS 2062 (Part 1):2025 Strong Match
IS 2062 (Part 1) E300B0 IS 2062 (Part 1):2025 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Mn Si S P CEV
<=0.20 <=1.40 <=0.40 <=0.045 <=0.045 <=0.39
Mechanical Properties
Tensile Strength >=360 MPa
Yield Strength 235 MPa (<=16mm) / 225 MPa (16-40mm) / 215 MPa (40-100mm) / 195 MPa (>100mm)
Elongation >=26% (<=40mm) / >=25% (40-63mm) / >=24% (63-100mm) / >=22% (>100mm)
Impact Energy >=27 J at room temperature (optional)

More data from IS 2062 (Part 1):2025

From the standard
Yield stress by thickness 4 thickness ranges
Thickness or diameter (mm)Yield stress ReH, min (MPa)
Up to 16235
Over 16 to 40225
Over 40 to 100215
Over 100195
For thickness or diameter above 100 mm, a lower minimum tensile strength may be agreed between the purchaser and the manufacturer.
Source: IS 2062 (Part 1):2025, Table 3, notes 1 and 4
Elongation by thickness gauge length 5.65 root So
Thickness or diameter (mm)Elongation A, min (%)
Up to 4026
Over 40 to 6325
Over 63 to 10024
Over 10022
Values are for lengthwise test pieces. For crosswise test pieces (plates, sheets and strips) up to 100 mm, the values are 2 lower.
Source: IS 2062 (Part 1):2025, Table 3, notes 5 and 6
Bend test t is the thickness
Internal bend diameter, maximum, thickness up to 25 mm
2t
Internal bend diameter, maximum, thickness over 25 to 30 mm
3t
t is the thickness or diameter of the test piece. The bend test is not required above 30 mm for grades E 235 to E 275.
Source: IS 2062 (Part 1):2025, Table 3, note 2
Impact test and deoxidation quality BR
Impact test
Optional; if required, at room temperature (23 +/- 5°C)
Minimum Charpy impact energy
27 J
Mode of deoxidation
Semi-killed or killed
Source: IS 2062 (Part 1):2025, Tables 1 and 3, clause 5
Other composition limits from the table notes
Nitrogen, maximum
0.012 percent
Copper as residual, maximum
0.20 percent
Micro-alloying elements (Nb, V, Ti), total maximum
0.25 percent
Alloying elements (Cr, Ni, Mo, B), by agreement, maximum
0.50 percent
Copper-bearing quality
Cu 0.20 to 0.35 percent by agreement, suffix Cu (for example E 250 Cu), CE limit raised by 0.02
Carbon equivalent CE = C + Mn/6 + (Cr+Mo+V)/5 + (Ni+Cu)/15, from the ladle analysis.
Source: IS 2062 (Part 1):2025, Table 1, notes 3 to 9

Active IS 2062 (Part 1):2025 E235BR Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 2062 (Part 1):2025 E235BR listings at this time.

Register for Alerts

Buyer RFQs for IS 2062 (Part 1):2025 E235BR

+ Post an RFQ for this grade

No open buyer requirements for IS 2062 (Part 1):2025 E235BR at this time.

Register for Alerts