IS 2062 (Part 1) E235C vs AS/NZS Grade 500

Strong Match — 95% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E235C (IS 2062 (Part 1):2025) and AS/NZS Grade 500 (AS/NZS 3597:2008) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E235C is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while AS/NZS Grade 500 is commonly used for heavy mining equipment, bulldozer blades, wear-resistant structural applications, large crane booms, offshore jackets.. IS 2062 (Part 1) E235C is defined under Bureau of Indian Standards (IS), originating from India, while AS/NZS Grade 500 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, IS 2062 (Part 1) E235C vs AS/NZS Grade 500 is a 95% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95%.

Frequently Compared With IS 2062 (Part 1) E235C:
IS 2062 (Part 1) E235B0 IS 2062 (Part 1) E235A IS 2062 (Part 1) E235BR GOST 19281 09G2S CSA G40.21 350W CSA G40.21 400A CSA G40.21 400W CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 480W
Match Breakdown
CHEMISTRY MATCH
95%
MECHANICAL MATCH
No shared data
OVERALL
95%
Specifications
Property IS 2062 (Part 1) E235C AS/NZS Grade 500
Standard IS 2062 (Part 1):2025 AS/NZS 3597:2008
Category Structural Steel Structural Steel
C (%) <=0.17 max 0.2
Mn (%) <=1.40 max 1.6
Si (%) <=0.40 max 0.55
S (%) <=0.040 max 0.03
P (%) <=0.040 max 0.03
CEV (%) <=0.38 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E235C AS/NZS Grade 500
Tensile Strength >=360 MPa Not specified
Yield Strength 235 MPa (<=16mm) / 225 MPa (16-40mm) / 215 MPa (40-100mm) / 195 MPa (>100mm) Not specified
Elongation >=26% (<=40mm) / >=25% (40-63mm) / >=24% (63-100mm) / >=22% (>100mm) Not specified
Impact Energy >=27 J at -20°C Not specified
Typical Applications
IS 2062 (Part 1) E235C
Structural work: welded, bolted and riveted structures and general engineering purposes
AS/NZS Grade 500
Heavy mining equipment, bulldozer blades, wear-resistant structural applications, large crane booms, offshore jackets.
Key Differences
Can IS 2062 (Part 1) E235C Be Substituted With AS/NZS Grade 500?
IS 2062 (Part 1) E235C and AS/NZS Grade 500 overlap closely enough on chemistry and mechanical properties that AS/NZS Grade 500 is often considered as a substitute for IS 2062 (Part 1) E235C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 2062 (Part 1) E235C
No active listings currently.
AS/NZS Grade 500
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3100–3600 mm (122.05–141.73 in)
On M-EX Right Now
IS 2062 (Part 1) E235C
0 active listings and RFQs →
AS/NZS Grade 500
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E235C and AS/NZS Grade 500?
IS 2062 (Part 1) E235C specifies CEV which is not specified for AS/NZS Grade 500.
Can IS 2062 (Part 1) E235C be substituted with AS/NZS Grade 500?
IS 2062 (Part 1) E235C and AS/NZS Grade 500 overlap closely enough on chemistry and mechanical properties that AS/NZS Grade 500 is often considered as a substitute for IS 2062 (Part 1) E235C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.