IS 2062 (Part 1) E275A vs IS 2062 (Part 1) E275C

Strong Match — 98.8% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E275A (IS 2062 (Part 1):2025) and IS 2062 (Part 1) E275C (IS 2062 (Part 1):2025) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E275A is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 (Part 1) E275C is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 (Part 1) E275A is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 (Part 1) E275C is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 (Part 1) E275A vs IS 2062 (Part 1) E275C is a 98.2% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98.8%.

Frequently Compared With IS 2062 (Part 1) E275A:
IS 2062 (Part 1) E250B0 IS 2062 (Part 1) E250A CSA G40.21 260W CSA G40.21 350W CSA G40.21 400A GOST 19281 09G2S AS/NZS 3679.1 300 CSA G40.21 400W AS/NZS 3679.1 350 CSA G40.21 300W CSA G40.21 480W ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
98.2%
MECHANICAL MATCH
100%
OVERALL
98.8%
Specifications
Property IS 2062 (Part 1) E275A IS 2062 (Part 1) E275C
Standard IS 2062 (Part 1):2025 IS 2062 (Part 1):2025
Category Structural Steel Structural Steel
C (%) <=0.23 <=0.20
Mn (%) <=1.50 <=1.50
Si (%) <=0.40 <=0.40
S (%) <=0.045 <=0.040
P (%) <=0.045 <=0.040
CEV (%) <=0.43 <=0.41
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E275A IS 2062 (Part 1) E275C
Tensile Strength >=430 MPa >=430 MPa
Yield Strength 275 MPa (<=16mm) / 265 MPa (16-40mm) / 255 MPa (40-100mm) / 225 MPa (>100mm) 275 MPa (<=16mm) / 265 MPa (16-40mm) / 255 MPa (40-100mm) / 225 MPa (>100mm)
Elongation >=23% (<=40mm) / >=22% (40-63mm) / >=21% (63-100mm) / >=19% (>100mm) >=23% (<=40mm) / >=22% (40-63mm) / >=21% (63-100mm) / >=19% (>100mm)
Impact not required Not specified
Impact Energy Not specified >=27 J at -20°C
Typical Applications
IS 2062 (Part 1) E275A
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 (Part 1) E275C
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 (Part 1) E275A Be Substituted With IS 2062 (Part 1) E275C?
IS 2062 (Part 1) E275A and IS 2062 (Part 1) E275C overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E275C is often considered as a substitute for IS 2062 (Part 1) E275A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 (Part 1) E275A
0 active listings and RFQs →
IS 2062 (Part 1) E275C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E275A and IS 2062 (Part 1) E275C?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 (Part 1) E275A be substituted with IS 2062 (Part 1) E275C?
IS 2062 (Part 1) E275A and IS 2062 (Part 1) E275C overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E275C is often considered as a substitute for IS 2062 (Part 1) E275A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.