IS 2062 (Part 1) E350A vs IS 2062 (Part 1) E410BR

Strong Match — 88.8% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E350A (IS 2062 (Part 1):2025) and IS 2062 (Part 1) E410BR (IS 2062 (Part 1):2025) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E350A is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 (Part 1) E410BR is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 (Part 1) E350A is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 (Part 1) E410BR is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 (Part 1) E350A vs IS 2062 (Part 1) E410BR is a 99.8% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a strong match overall at 88.8%.

Frequently Compared With IS 2062 (Part 1) E350A:
CSA G40.21 350W GOST 19281 09G2S CSA G40.21 300W ASTM A1008 SS Grade 50 CSA G40.21 260W CSA G40.21 400W ASTM A572 Gr.65 AS/NZS 3679.1 300 AS/NZS 3679.1 350 CSA G40.21 400A CSA G40.21 480W ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
99.8%
MECHANICAL MATCH
66.7%
OVERALL
88.8%
Specifications
Property IS 2062 (Part 1) E350A IS 2062 (Part 1) E410BR
Standard IS 2062 (Part 1):2025 IS 2062 (Part 1):2025
Category Structural Steel Structural Steel
C (%) <=0.22 <=0.22
Mn (%) <=1.60 <=1.65
Si (%) <=0.45 <=0.45
S (%) <=0.045 <=0.045
P (%) <=0.045 <=0.045
CEV (%) <=0.47 <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E350A IS 2062 (Part 1) E410BR
Tensile Strength >=490 MPa >=540 MPa
Yield Strength 350 MPa (<=16mm) / 330 MPa (16-40mm) / 320 MPa (40-100mm) / 290 MPa (>100mm) 410 MPa (<=16mm) / 390 MPa (16-40mm) / 380 MPa (40-100mm) / 350 MPa (>100mm)
Elongation >=22% (<=40mm) / >=21% (40-63mm) / >=20% (63-100mm) / >=18% (>100mm) >=20% (<=40mm) / >=19% (40-63mm) / >=18% (63-100mm) / >=18% (>100mm)
Impact not required Not specified
Impact Energy Not specified >=25 J at room temperature (optional)
Typical Applications
IS 2062 (Part 1) E350A
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 (Part 1) E410BR
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 (Part 1) E350A Be Substituted With IS 2062 (Part 1) E410BR?
IS 2062 (Part 1) E350A and IS 2062 (Part 1) E410BR overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E410BR is often considered as a substitute for IS 2062 (Part 1) E350A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 (Part 1) E350A
0 active listings and RFQs →
IS 2062 (Part 1) E410BR
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E350A and IS 2062 (Part 1) E410BR?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 (Part 1) E350A be substituted with IS 2062 (Part 1) E410BR?
IS 2062 (Part 1) E350A and IS 2062 (Part 1) E410BR overlap closely enough on chemistry and mechanical properties that IS 2062 (Part 1) E410BR is often considered as a substitute for IS 2062 (Part 1) E350A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.