IS 2062 (Part 1) E410B0 vs ASTM A572 Gr.65

Related Material — 61.9% match based on chemical composition and mechanical property overlap.

IS 2062 (Part 1) E410B0 (IS 2062 (Part 1):2025) and ASTM A572 Gr.65 (ASTM A572) are both steel grades. Both fall under the Structural Steel category. IS 2062 (Part 1) E410B0 is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while ASTM A572 Gr.65 is commonly used for used for bridges, buildings, transmission towers, construction equipment, offshore structures, and structural members.. IS 2062 (Part 1) E410B0 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A572 Gr.65 is defined under ASTM International, originating from United States.

As per chemical composition, IS 2062 (Part 1) E410B0 vs ASTM A572 Gr.65 is a 92.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 61.9%.

Frequently Compared With IS 2062 (Part 1) E410B0:
CSA G40.21 350W GOST 19281 09G2S AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 400A ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 CSA G40.21 260W AS/NZS 3679.1 350 CSA G40.21 480W ASTM A283C CSA G40.21 400W
Match Breakdown
CHEMISTRY MATCH
92.8%
MECHANICAL MATCH
0%
OVERALL
61.9%
Specifications
Property IS 2062 (Part 1) E410B0 ASTM A572 Gr.65
Standard IS 2062 (Part 1):2025 ASTM A572
Category Structural Steel Structural Steel
C (%) <=0.20 0.23 max
Mn (%) <=1.65 1.35 max
Si (%) <=0.45 0.40 max
S (%) <=0.045 0.050 max
P (%) <=0.045 0.040 max
CEV (%) <=0.50 Not specified
V (%) Not specified 0.15 max
Nb (%) Not specified 0.05 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 (Part 1) E410B0 ASTM A572 Gr.65
Tensile Strength >=540 MPa 550-690 MPa
Yield Strength 410 MPa (<=16mm) / 390 MPa (16-40mm) / 380 MPa (40-100mm) / 350 MPa (>100mm) 450 MPa min
Elongation >=20% (<=40mm) / >=19% (40-63mm) / >=18% (63-100mm) / >=18% (>100mm) 18-21%
Impact Energy >=25 J at 0°C Not specified
Hardness Not specified 170-220 HB
Typical Applications
IS 2062 (Part 1) E410B0
Structural work: welded, bolted and riveted structures and general engineering purposes
ASTM A572 Gr.65
Used for bridges, buildings, transmission towers, construction equipment, offshore structures, and structural members.
Key Differences
Can IS 2062 (Part 1) E410B0 Be Substituted With ASTM A572 Gr.65?
IS 2062 (Part 1) E410B0 and ASTM A572 Gr.65 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 2062 (Part 1) E410B0
No active listings currently.
ASTM A572 Gr.65
Plate → (4 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2600–4400 mm (102.36–173.23 in)
On M-EX Right Now
IS 2062 (Part 1) E410B0
0 active listings and RFQs →
ASTM A572 Gr.65
4 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 (Part 1) E410B0 and ASTM A572 Gr.65?
IS 2062 (Part 1) E410B0 specifies CEV which is not specified for ASTM A572 Gr.65. ASTM A572 Gr.65 specifies V, Nb which are not specified for IS 2062 (Part 1) E410B0.
Can IS 2062 (Part 1) E410B0 be substituted with ASTM A572 Gr.65?
IS 2062 (Part 1) E410B0 and ASTM A572 Gr.65 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.