IS 2062 E250C vs AS/NZS 3679.1 350

Related Material — 64.9% match based on chemical composition and mechanical property overlap.

IS 2062 E250C (IS 2062:2006) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. IS 2062 E250C is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. IS 2062 E250C is defined under Bureau of Indian Standards (IS), originating from India, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, IS 2062 E250C vs AS/NZS 3679.1 350 is a 97.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 64.9%.

Frequently Compared With IS 2062 E250C:
IS 2062 E250A CSA G40.21 260W CSA G40.21 400A CSA G40.21 480W IS 2062 E250B IS 2062 E250BR GOST 19281 09G2S CSA G40.21 300W CSA G40.21 350W CSA G40.21 400W ASTM A1008 SS Grade 50 IS 2062 E250B0
Match Breakdown
CHEMISTRY MATCH
97.4%
MECHANICAL MATCH
0%
OVERALL
64.9%
Specifications
Property IS 2062 E250C AS/NZS 3679.1 350
Standard IS 2062:2006 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.22
Mn (%) <=1.50 <=1.70
S (%) <=0.040 <=0.040
P (%) <=0.040 <=0.040
Si (%) <=0.40 <=0.50
CEV (%) <=0.39 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E250C AS/NZS 3679.1 350
Tensile Strength >=410 MPa 480-640 MPa
Yield Strength 250 MPa (<20mm) / 240 MPa (20-40mm) / 230 MPa (>40mm) 350 MPa min
Elongation >=23% 20% min
Impact Energy >=27 J at room temperature (25 +/- 2°C) Not specified
Typical Applications
IS 2062 E250C
Structural work: welded, bolted and riveted structures and general engineering purposes
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can IS 2062 E250C Be Substituted With AS/NZS 3679.1 350?
IS 2062 E250C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 2062 E250C
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
IS 2062 E250C
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E250C and AS/NZS 3679.1 350?
IS 2062 E250C specifies CEV which is not specified for AS/NZS 3679.1 350.
Can IS 2062 E250C be substituted with AS/NZS 3679.1 350?
IS 2062 E250C and AS/NZS 3679.1 350 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.