IS 2062 E410B0 vs GOST 19281 09G2S

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 2062 E410B0 (IS 2062:2009) and GOST 19281 09G2S (GOST 19281-2014) are both steel grades. Both fall under the Structural Steel category. IS 2062 E410B0 is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while GOST 19281 09G2S is commonly used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.. IS 2062 E410B0 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 2062 E410B0 vs GOST 19281 09G2S is a 65.5% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 2062 E410B0:
CSA G40.21 400A ASTM A283C CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W CSA G40.21 480W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80 CSA G40.21 350W CSA G40.21 400W AS/NZS 3679.1 350 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
65.5%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 2062 E410B0 GOST 19281 09G2S
Standard IS 2062:2009 GOST 19281-2014
Category Structural Steel Structural Steel
C (%) <=0.20 0.07-0.12
Mn (%) <=1.60 1.3-1.7
S (%) <=0.045 0.04 max
P (%) <=0.045 0.035 max
Si (%) <=0.45 0.5-0.8
CEV (%) <=0.46 Not specified
Ni (%) Not specified 0.3 max
Cr (%) Not specified 0.3 max
Cu (%) Not specified 0.3 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E410B0 GOST 19281 09G2S
Tensile Strength >=540 MPa 490-640 MPa
Yield Strength 410 MPa (<20mm) / 390 MPa (20-40mm) / 380 MPa (>40mm) 345 MPa min
Elongation >=20% 21% min
Impact Energy >=25 J at 0°C Not specified
Hardness Not specified 140-190 HB
Typical Applications
IS 2062 E410B0
Structural work: welded, bolted and riveted structures and general engineering purposes
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
Key Differences
Can IS 2062 E410B0 Be Substituted With GOST 19281 09G2S?
IS 2062 E410B0 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 2062 E410B0
No active listings currently.
GOST 19281 09G2S
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3800 mm (114.17–149.61 in)
On M-EX Right Now
IS 2062 E410B0
0 active listings and RFQs →
GOST 19281 09G2S
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E410B0 and GOST 19281 09G2S?
IS 2062 E410B0 specifies CEV which is not specified for GOST 19281 09G2S. GOST 19281 09G2S specifies Ni, Cr, Cu which are not specified for IS 2062 E410B0.
Can IS 2062 E410B0 be substituted with GOST 19281 09G2S?
IS 2062 E410B0 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.