IS 2062 E410C vs IS 2062 E410

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 2062 E410C (IS 2062:2009) and IS 2062 E410 (IS 2062:2006) are both steel grades. Both fall under the Structural Steel category. IS 2062 E410C is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 E410 is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 E410C is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E410 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E410C vs IS 2062 E410 is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 2062 E410C:
AS/NZS 3679.1 350 CSA G40.21 400A CSA G40.21 480W ASTM A283C GOST 19281 09G2S AS/NZS 3679.1 300 CSA G40.21 400W CSA G40.21 260W ASTM A1008 SS Grade 50 ASTM A572 Gr.65 CSA G40.21 300W CSA G40.21 350W
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 2062 E410C IS 2062 E410
Standard IS 2062:2009 IS 2062:2006
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.20
Mn (%) <=1.60 <=1.60
S (%) <=0.045 <=0.045
P (%) <=0.045 <=0.045
Si (%) <=0.45 <=0.45
CEV (%) <=0.46 <=0.44
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E410C IS 2062 E410
Tensile Strength >=540 MPa >=540 MPa
Yield Strength 410 MPa (<20mm) / 390 MPa (20-40mm) / 380 MPa (>40mm) 410 MPa (<20mm) / 390 MPa (20-40mm) / 380 MPa (>40mm)
Elongation >=20% >=20%
Impact Energy >=25 J at -20°C >=50 J at room temperature (25 +/- 2°C) / >=25 J at -20°C
Typical Applications
IS 2062 E410C
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 E410
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 E410C Be Substituted With IS 2062 E410?
IS 2062 E410C and IS 2062 E410 overlap closely enough on chemistry and mechanical properties that IS 2062 E410 is often considered as a substitute for IS 2062 E410C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 E410C
0 active listings and RFQs →
IS 2062 E410
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E410C and IS 2062 E410?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E410C be substituted with IS 2062 E410?
IS 2062 E410C and IS 2062 E410 overlap closely enough on chemistry and mechanical properties that IS 2062 E410 is often considered as a substitute for IS 2062 E410C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.