IS 2062 E450B0 vs ASTM A283C

Related Material — 63.5% match based on chemical composition and mechanical property overlap.

IS 2062 E450B0 (IS 2062:2009) and ASTM A283C (ASTM A283) are both steel grades. Both fall under the Structural Steel category. IS 2062 E450B0 is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while ASTM A283C is commonly used for used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.. IS 2062 E450B0 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A283C is defined under ASTM International, originating from United States.

As per chemical composition, IS 2062 E450B0 vs ASTM A283C is a 95.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 63.5%.

Frequently Compared With IS 2062 E450B0:
AS/NZS 3679.1 300 CSA G40.21 350W CSA G40.21 400A ASTM A1008 SS Grade 50 CSA G40.21 260W CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 80 GOST 19281 09G2S ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
95.2%
MECHANICAL MATCH
0%
OVERALL
63.5%
Specifications
Property IS 2062 E450B0 ASTM A283C
Standard IS 2062:2009 ASTM A283
Category Structural Steel Structural Steel
C (%) <=0.22 0.24 max
Mn (%) <=1.60 0.90 max
S (%) <=0.045 0.040 max
P (%) <=0.045 0.035 max
Si (%) <=0.45 0.40 max
CEV (%) <=0.48 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E450B0 ASTM A283C
Tensile Strength >=570 MPa 380-515 MPa
Yield Strength 450 MPa (<20mm) / 430 MPa (20-40mm) / 420 MPa (>40mm) 205 MPa min
Elongation >=20% 23-27%
Impact Energy >=20 J at 0°C Not specified
Hardness Not specified 120-170 HB
Typical Applications
IS 2062 E450B0
Structural work: welded, bolted and riveted structures and general engineering purposes
ASTM A283C
Used for structural fabrication, storage tanks, buildings, bridges, machinery bases, and welded structures.
Key Differences
Can IS 2062 E450B0 Be Substituted With ASTM A283C?
IS 2062 E450B0 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 2062 E450B0
No active listings currently.
ASTM A283C
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3700 mm (114.17–145.67 in)
On M-EX Right Now
IS 2062 E450B0
0 active listings and RFQs →
ASTM A283C
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E450B0 and ASTM A283C?
IS 2062 E450B0 specifies CEV which is not specified for ASTM A283C.
Can IS 2062 E450B0 be substituted with ASTM A283C?
IS 2062 E450B0 and ASTM A283C share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.