IS 2062 E300C vs IS 2062 E300C

Strong Match — 99.1% match based on chemical composition and mechanical property overlap.

IS 2062 E300C (IS 2062:2011) and IS 2062 E300C (IS 2062:2009) are both steel grades. Both fall under the Structural Steel category. IS 2062 E300C is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 E300C is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 E300C is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E300C is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E300C vs IS 2062 E300C is a 98.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 99.1%.

Frequently Compared With IS 2062 E300C:
AS/NZS 3679.1 300 ASTM A1008 SS Grade 50 CSA G40.21 300W CSA G40.21 400W ASTM A283C GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A CSA G40.21 480W ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
98.6%
MECHANICAL MATCH
100%
OVERALL
99.1%
Specifications
Property IS 2062 E300C IS 2062 E300C
Standard IS 2062:2011 IS 2062:2009
Category Structural Steel Structural Steel
C (%) <=0.20 <=0.20
Mn (%) <=1.50 <=1.30
Si (%) <=0.45 <=0.45
S (%) <=0.040 <=0.045
P (%) <=0.040 <=0.045
CEV (%) <=0.44 <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E300C IS 2062 E300C
Tensile Strength >=440 MPa >=440 MPa
Yield Strength 300 MPa (<=20mm) / 290 MPa (20-40mm) / 280 MPa (>40mm) 300 MPa (<20mm) / 290 MPa (20-40mm) / 280 MPa (>40mm)
Elongation >=22% >=22%
Impact Energy >=27 J at -20°C >=27 J at -20°C
Typical Applications
IS 2062 E300C
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 E300C
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 E300C Be Substituted With IS 2062 E300C?
IS 2062 E300C and IS 2062 E300C overlap closely enough on chemistry and mechanical properties that IS 2062 E300C is often considered as a substitute for IS 2062 E300C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 E300C
0 active listings and RFQs →
IS 2062 E300C
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E300C and IS 2062 E300C?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E300C be substituted with IS 2062 E300C?
IS 2062 E300C and IS 2062 E300C overlap closely enough on chemistry and mechanical properties that IS 2062 E300C is often considered as a substitute for IS 2062 E300C in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.