Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 2062 E650A (IS 2062:2011) and IS 2062 E650A (IS 2062:2009) are both steel grades. Both fall under the Structural Steel category. IS 2062 E650A is typically used for structural work: welded, bolted and riveted structures and general engineering purposes, while IS 2062 E650A is commonly used for structural work: welded, bolted and riveted structures and general engineering purposes. IS 2062 E650A is defined under Bureau of Indian Standards (IS), originating from India, while IS 2062 E650A is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 2062 E650A vs IS 2062 E650A is a 100% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 2062 E650A:
ASTM A1008 SS Grade 50 ASTM A283C GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 480W ASTM A1008 SS Grade 80 CSA G40.21 400A CSA G40.21 400W
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
100%
OVERALL
100%
Specifications
Property IS 2062 E650A IS 2062 E650A
Standard IS 2062:2011 IS 2062:2009
Category Structural Steel Structural Steel
C (%) <=0.22 <=0.22
Mn (%) <=1.70 <=1.70
Si (%) <=0.50 <=0.50
S (%) <=0.015 <=0.015
P (%) <=0.025 <=0.025
CEV (%) <=0.55 <=0.52
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 2062 E650A IS 2062 E650A
Tensile Strength >=780 MPa >=780 MPa
Yield Strength 650 MPa (<=20mm) / 630 MPa (20-40mm) / 620 MPa (>40mm) 650 MPa (<20mm) / 630 MPa (20-40mm) / 620 MPa (>40mm)
Elongation >=12% >=12%
Impact not required not required
Typical Applications
IS 2062 E650A
Structural work: welded, bolted and riveted structures and general engineering purposes
IS 2062 E650A
Structural work: welded, bolted and riveted structures and general engineering purposes
Can IS 2062 E650A Be Substituted With IS 2062 E650A?
IS 2062 E650A and IS 2062 E650A overlap closely enough on chemistry and mechanical properties that IS 2062 E650A is often considered as a substitute for IS 2062 E650A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 2062 E650A
0 active listings and RFQs →
IS 2062 E650A
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 2062 E650A and IS 2062 E650A?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 2062 E650A be substituted with IS 2062 E650A?
IS 2062 E650A and IS 2062 E650A overlap closely enough on chemistry and mechanical properties that IS 2062 E650A is often considered as a substitute for IS 2062 E650A in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.