IS 3195 50Cr4V2 vs IS 3195 60Cr4V2

Strong Match — 90.7% match based on chemical composition and mechanical property overlap.

IS 3195 50Cr4V2 (IS 3195:1992) and IS 3195 60Cr4V2 (IS 3195:1992) are both steel grades. Both fall under the Spring Steel category. IS 3195 50Cr4V2 is typically used for volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword), while IS 3195 60Cr4V2 is commonly used for volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword). IS 3195 50Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 3195 60Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 3195 50Cr4V2 vs IS 3195 60Cr4V2 is a 86.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 90.7%.

Frequently Compared With IS 3195 50Cr4V2:
IS 3431 55Si7 IS 3431 60Cr4V2 IS 5517 55Cr3 IS 3195 113C6 IS 3195 52Cr4Mo2V IS 3431 50Cr4V2 IS 3195 98C6 GB/T 1222 55CrMnA IS 3195 55Si7 IS 3195 60Si7 EN 10089 50CrV4 EN 10083-1 51CrV4
Match Breakdown
CHEMISTRY MATCH
86.1%
MECHANICAL MATCH
100%
OVERALL
90.7%
Specifications
Property IS 3195 50Cr4V2 IS 3195 60Cr4V2
Standard IS 3195:1992 IS 3195:1992
Category Spring Steel Spring Steel
C (%) 0.45-0.55 0.55-0.65
Cr (%) 0.90-1.20 0.90-1.20
Mn (%) 0.50-0.80 0.80-1.00
P (%) <=0.030 <=0.030
S (%) <=0.030 <=0.030
Si (%) 0.15-0.35 0.15-0.35
V (%) 0.15-0.30 0.15-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 3195 50Cr4V2 IS 3195 60Cr4V2
Hardness, annealed <=245 HB <=255 HB
Hardness, untreated (hot rolled) about 310 HB (for guidance only) about 310 HB (for guidance only)
Typical Applications
IS 3195 50Cr4V2
Volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword)
IS 3195 60Cr4V2
Volute and helical springs for railway rolling stock; flats and rounds, springs worked hot and heat-treated (clause 1.1, foreword)
Can IS 3195 50Cr4V2 Be Substituted With IS 3195 60Cr4V2?
IS 3195 50Cr4V2 and IS 3195 60Cr4V2 overlap closely enough on chemistry and mechanical properties that IS 3195 60Cr4V2 is often considered as a substitute for IS 3195 50Cr4V2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 3195 50Cr4V2
0 active listings and RFQs →
IS 3195 60Cr4V2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 3195 50Cr4V2 and IS 3195 60Cr4V2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 3195 50Cr4V2 be substituted with IS 3195 60Cr4V2?
IS 3195 50Cr4V2 and IS 3195 60Cr4V2 overlap closely enough on chemistry and mechanical properties that IS 3195 60Cr4V2 is often considered as a substitute for IS 3195 50Cr4V2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.