IS 3748 T135Cr2 vs IS 3748 133T3

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 3748 T135Cr2 (IS 3748:1990) and IS 3748 133T3 (IS 3748:1990) are both steel grades. Both fall under the Tool & Die Steels category. IS 3748 T135Cr2 is typically used for cold work tools and dies for blanking, trimming, chipping and shearing, while IS 3748 133T3 is commonly used for cold work tools and dies for blanking, trimming, chipping and shearing. IS 3748 T135Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 3748 133T3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 3748 T135Cr2 vs IS 3748 133T3 is a 86.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 3748 T135Cr2:
EN ISO 683-17 100Cr6 IS 3748 118T3 EN ISO 4957 1.2316 DIN EN ISO 4957 1.2344 DIN EN ISO 4957 1.2379 IS 3748 103T3 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 133T3 GOST 5950 3H2W8F GB/T 1299 4Cr5MoSiV IS 1570 (Part 6) 118T3 GB/T 1299 3Cr2W8V
Match Breakdown
CHEMISTRY MATCH
86.6%
MECHANICAL MATCH
100%
OVERALL
35%
Specifications
Property IS 3748 T135Cr2 IS 3748 133T3
Standard IS 3748:1990 IS 3748:1990
Category Tool & Die Steels Tool & Die Steels
C (%) 1.25-1.40 1.25-1.40
Si (%) 0.10-0.30 0.10-0.30
Mn (%) <=0.40 <=0.40
Cr (%) 0.30-0.60 Not specified
V (%) <=0.30 Not specified
S (%) <=0.035 <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 3748 T135Cr2 IS 3748 133T3
Hardness <=220 HB <=220 HB
Condition Annealed (maximum Brinell hardness) Annealed (maximum Brinell hardness)
Typical Applications
IS 3748 T135Cr2
Cold work tools and dies for blanking, trimming, chipping and shearing
IS 3748 133T3
Cold work tools and dies for blanking, trimming, chipping and shearing
Key Differences
Can IS 3748 T135Cr2 Be Substituted With IS 3748 133T3?
IS 3748 T135Cr2 and IS 3748 133T3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 3748 T135Cr2
0 active listings and RFQs →
IS 3748 133T3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 3748 T135Cr2 and IS 3748 133T3?
IS 3748 T135Cr2 specifies Cr, V which are not specified for IS 3748 133T3. IS 3748 133T3 specifies P which is not specified for IS 3748 T135Cr2.
Can IS 3748 T135Cr2 be substituted with IS 3748 133T3?
IS 3748 T135Cr2 and IS 3748 133T3 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.