IS 3748 XT35Cr5Mo1V3 vs DIN EN ISO 4957 1.2344

Minimal Match — 54.5% match based on chemical composition and mechanical property overlap.

IS 3748 XT35Cr5Mo1V3 (IS 3748:1990) and DIN EN ISO 4957 1.2344 (DIN EN ISO 4957:2018-11) are both steel grades. Both fall under the Tool & Die Steels category. IS 3748 XT35Cr5Mo1V3 is typically used for hot work tools and dies, such as die-casting dies and hot headers, while DIN EN ISO 4957 1.2344 is commonly used for die casting dies, extrusion dies, forging dies, hot shear blades, mandrels, pressure die casting tooling. IS 3748 XT35Cr5Mo1V3 is defined under Bureau of Indian Standards (IS), originating from India, while DIN EN ISO 4957 1.2344 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 3748 XT35Cr5Mo1V3 vs DIN EN ISO 4957 1.2344 is a 81.7% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 54.5%.

Frequently Compared With IS 3748 XT35Cr5Mo1V3:
GB/T 1299 4Cr5MoSiV GB/T 1299 4Cr5MoSiV1 IS 3748 118T3 EN ISO 4957 1.2316 DIN EN ISO 4957 1.2379 EN ISO 683-17 100Cr6 IS 1570 (Part 6) 103T3 IS 1570 (Part 6) 118T3 IS 1570 (Part 6) 133T3 GB/T 1299 3Cr2W8V IS 3748 103T3 IS 3748 133T3
Match Breakdown
CHEMISTRY MATCH
81.7%
MECHANICAL MATCH
0%
OVERALL
54.5%
Specifications
Property IS 3748 XT35Cr5Mo1V3 DIN EN ISO 4957 1.2344
Standard IS 3748:1990 DIN EN ISO 4957:2018-11
Category Tool & Die Steels Tool & Die Steels
C (%) 0.30-0.40 0.37–0.43
Si (%) 0.80-1.20 0.90–1.20
Mn (%) 0.25-0.50 0.30–0.50
Cr (%) 4.75-5.50 4.80–5.50
Mo (%) 1.20-1.60 1.20–1.50
V (%) 0.20-0.40 0.90–1.10
S (%) <=0.035 ≤0.030
P (%) <=0.035 ≤0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 3748 XT35Cr5Mo1V3 DIN EN ISO 4957 1.2344
Hardness <=235 HB Not specified
Condition Annealed (maximum Brinell hardness) Not specified
Hardness (annealed) Not specified ≤229 HB
Hardness (hardened) Not specified 44–52 HRC
Tensile Strength Not specified 1200–1600 MPa
Elongation Not specified ≥8%
Typical Applications
IS 3748 XT35Cr5Mo1V3
Hot work tools and dies, such as die-casting dies and hot headers
DIN EN ISO 4957 1.2344
Die casting dies, extrusion dies, forging dies, hot shear blades, mandrels, pressure die casting tooling
Can IS 3748 XT35Cr5Mo1V3 Be Substituted With DIN EN ISO 4957 1.2344?
IS 3748 XT35Cr5Mo1V3 and DIN EN ISO 4957 1.2344 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 3748 XT35Cr5Mo1V3
No active listings currently.
DIN EN ISO 4957 1.2344
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3000–3700 mm (118.11–145.67 in)
On M-EX Right Now
IS 3748 XT35Cr5Mo1V3
0 active listings and RFQs →
DIN EN ISO 4957 1.2344
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 3748 XT35Cr5Mo1V3 and DIN EN ISO 4957 1.2344?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 3748 XT35Cr5Mo1V3 be substituted with DIN EN ISO 4957 1.2344?
IS 3748 XT35Cr5Mo1V3 and DIN EN ISO 4957 1.2344 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.