IS 4367 15Ni16Cr5 vs IS 11169 (Part 1) 15Ni16Cr5

Strong Match — 87.7% match based on chemical composition and mechanical property overlap.

IS 4367 15Ni16Cr5 (IS 4367:1991) and IS 11169 (Part 1) 15Ni16Cr5 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. IS 4367 15Ni16Cr5 is typically used for aircraft gears, heavy duty gears, transmission shafts, camshafts, automotive components, while IS 11169 (Part 1) 15Ni16Cr5 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). IS 4367 15Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 15Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 15Ni16Cr5 vs IS 11169 (Part 1) 15Ni16Cr5 is a 98.3% match. As per mechanical properties, the match is 66.7%. Combined, this makes them a strong match overall at 87.7%.

Frequently Compared With IS 4367 15Ni16Cr5:
GOST 4543 12HN3A NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
66.7%
OVERALL
87.7%
Specifications
Property IS 4367 15Ni16Cr5 IS 11169 (Part 1) 15Ni16Cr5
Standard IS 4367:1991 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 3.80-4.30 3.80-4.30
Cr (%) 1.00-1.40 1.00-1.40
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 15Ni16Cr5 IS 11169 (Part 1) 15Ni16Cr5
Tensile Strength 1350 MPa min Not specified
Elongation >=9% Not specified
Izod Impact 35 J min Not specified
Hardness (soft annealed) <=241 HB Not specified
Condition Refined, quenched and stress relieved (core properties), ruling section up to 30 mm Not specified
Core Tensile Strength Not specified >=1350 MPa (30 mm) / >=1200 MPa (60 mm) / >=1150 MPa (90 mm)
Core Elongation Not specified >=9% (30 mm)
Hardness, annealed Not specified <=200 HB
Typical Applications
IS 4367 15Ni16Cr5
aircraft gears, heavy duty gears, transmission shafts, camshafts, automotive components
IS 11169 (Part 1) 15Ni16Cr5
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can IS 4367 15Ni16Cr5 Be Substituted With IS 11169 (Part 1) 15Ni16Cr5?
IS 4367 15Ni16Cr5 and IS 11169 (Part 1) 15Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni16Cr5 is often considered as a substitute for IS 4367 15Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 4367 15Ni16Cr5
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5500–6000 mm (216.54–236.22 in)
IS 11169 (Part 1) 15Ni16Cr5
No active listings currently.
On M-EX Right Now
IS 4367 15Ni16Cr5
2 active listings and RFQs →
IS 11169 (Part 1) 15Ni16Cr5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 15Ni16Cr5 and IS 11169 (Part 1) 15Ni16Cr5?
IS 4367 15Ni16Cr5 specifies S, P which are not specified for IS 11169 (Part 1) 15Ni16Cr5.
Can IS 4367 15Ni16Cr5 be substituted with IS 11169 (Part 1) 15Ni16Cr5?
IS 4367 15Ni16Cr5 and IS 11169 (Part 1) 15Ni16Cr5 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni16Cr5 is often considered as a substitute for IS 4367 15Ni16Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.