IS 4367 10Cr9Mo10 vs IS 1570 (Part 4) 07Cr4Mo6

Close Alternative — 77% match based on chemical composition and mechanical property overlap.

IS 4367 10Cr9Mo10 (IS 4367:1991) and IS 1570 (Part 4) 07Cr4Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 10Cr9Mo10 vs IS 1570 (Part 4) 07Cr4Mo6 is a 77% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77%.

Frequently Compared With IS 4367 10Cr9Mo10:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Cr36Mo10H UNI 11234 100Cr6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 NF A35-565 100C6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 7) 12Cr4Mo5H IS 1570 (Part 4) 103Cr6
Match Breakdown
CHEMISTRY MATCH
77%
MECHANICAL MATCH
No shared data
OVERALL
77%
Specifications
Property IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6
Standard IS 4367:1991 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) <=0.15 <=0.12
Si (%) <=0.50 0.15-0.60
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 2.00-2.50 0.70-1.10
Mo (%) 0.90-1.10 0.45-0.65
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6
Tensile Strength 410-590 MPa Not specified
Yield Strength 245 MPa min Not specified
Elongation >=18% Not specified
Izod Impact 55 J min Not specified
Hardness (soft annealed) <=187 HB Not specified
Condition Normalised and tempered, ruling section up to 50 mm Not specified
Key Differences
Can IS 4367 10Cr9Mo10 Be Substituted With IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 10Cr9Mo10 and IS 1570 (Part 4) 07Cr4Mo6 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 4367 10Cr9Mo10
0 active listings and RFQs →
IS 1570 (Part 4) 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 10Cr9Mo10 and IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 10Cr9Mo10 specifies S, P which are not specified for IS 1570 (Part 4) 07Cr4Mo6.
Can IS 4367 10Cr9Mo10 be substituted with IS 1570 (Part 4) 07Cr4Mo6?
IS 4367 10Cr9Mo10 and IS 1570 (Part 4) 07Cr4Mo6 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.