IS 4367 15Ni5Cr4Mo1 vs IS 1570 (Part 4) 15Ni5Cr4Mo1

Close Alternative — 81.4% match based on chemical composition and mechanical property overlap.

IS 4367 15Ni5Cr4Mo1 (IS 4367:1991) and IS 1570 (Part 4) 15Ni5Cr4Mo1 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 4367 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 15Ni5Cr4Mo1 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 15Ni5Cr4Mo1 vs IS 1570 (Part 4) 15Ni5Cr4Mo1 is a 97.1% match. As per mechanical properties, the match is 50%. Combined, this makes them a close alternative overall at 81.4%.

Frequently Compared With IS 4367 15Ni5Cr4Mo1:
IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 12Cr2Mo5V2H IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
97.1%
MECHANICAL MATCH
50%
OVERALL
81.4%
Specifications
Property IS 4367 15Ni5Cr4Mo1 IS 1570 (Part 4) 15Ni5Cr4Mo1
Standard IS 4367:1991 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.60-1.00 0.60-1.00
Ni (%) 1.00-1.50 1.00-1.50
Cr (%) 0.75-1.25 0.75-1.25
Mo (%) 0.08-0.15 0.08-0.15
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 15Ni5Cr4Mo1 IS 1570 (Part 4) 15Ni5Cr4Mo1
Tensile Strength 1000 MPa min >=990 MPa
Elongation >=9% >=9%
Izod Impact 41 J min >=41 J
Hardness (soft annealed) <=217 HB Not specified
Condition Refined, quenched and stress relieved (core properties), ruling section up to 30 mm Case hardening steel, refined and quenched, core properties
Key Differences
Can IS 4367 15Ni5Cr4Mo1 Be Substituted With IS 1570 (Part 4) 15Ni5Cr4Mo1?
IS 4367 15Ni5Cr4Mo1 and IS 1570 (Part 4) 15Ni5Cr4Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 4367 15Ni5Cr4Mo1
0 active listings and RFQs →
IS 1570 (Part 4) 15Ni5Cr4Mo1
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 15Ni5Cr4Mo1 and IS 1570 (Part 4) 15Ni5Cr4Mo1?
IS 4367 15Ni5Cr4Mo1 specifies S, P which are not specified for IS 1570 (Part 4) 15Ni5Cr4Mo1.
Can IS 4367 15Ni5Cr4Mo1 be substituted with IS 1570 (Part 4) 15Ni5Cr4Mo1?
IS 4367 15Ni5Cr4Mo1 and IS 1570 (Part 4) 15Ni5Cr4Mo1 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.