IS 4367 50Cr4V2 vs IS 1570 (Part 4) 10Mo6

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 4367 50Cr4V2 (IS 4367:1991) and IS 1570 (Part 4) 10Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 4367 50Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 10Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 50Cr4V2 vs IS 1570 (Part 4) 10Mo6 is a 53.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 4367 50Cr4V2:
IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 12Cr2Mo5V2H
Match Breakdown
CHEMISTRY MATCH
53.4%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 4367 50Cr4V2 IS 1570 (Part 4) 10Mo6
Standard IS 4367:1991 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.45-0.55 <=0.15
Si (%) 0.10-0.35 0.15-0.25
Mn (%) 0.50-0.80 0.40-0.70
Cr (%) 0.90-1.20 <=0.25
V (%) 0.15-0.30 Not specified
S (%) <=0.035 Not specified
P (%) <=0.035 Not specified
Ni (%) Not specified <=0.30
Mo (%) Not specified 0.45-0.65
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 50Cr4V2 IS 1570 (Part 4) 10Mo6
Tensile Strength 900-1100 MPa Not specified
Yield Strength 700 MPa min Not specified
Elongation >=12% Not specified
Izod Impact 45 J min Not specified
Hardness 266-325 HB Not specified
Hardness (soft annealed) <=240 HB Not specified
Condition Hardened and tempered, ruling section up to 100 mm Not specified
Key Differences
Can IS 4367 50Cr4V2 Be Substituted With IS 1570 (Part 4) 10Mo6?
IS 4367 50Cr4V2 and IS 1570 (Part 4) 10Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 4367 50Cr4V2
0 active listings and RFQs →
IS 1570 (Part 4) 10Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 50Cr4V2 and IS 1570 (Part 4) 10Mo6?
IS 4367 50Cr4V2 specifies V, S, P which are not specified for IS 1570 (Part 4) 10Mo6. IS 1570 (Part 4) 10Mo6 specifies Ni, Mo which are not specified for IS 4367 50Cr4V2.
Can IS 4367 50Cr4V2 be substituted with IS 1570 (Part 4) 10Mo6?
IS 4367 50Cr4V2 and IS 1570 (Part 4) 10Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.