IS 4367 40Ni6Cr4Mo3 vs IS 4367 07Cr4Mo6

Minimal Match — 43.4% match based on chemical composition and mechanical property overlap.

IS 4367 40Ni6Cr4Mo3 (IS 4367:1991) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 4367 40Ni6Cr4Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 4367 40Ni6Cr4Mo3 vs IS 4367 07Cr4Mo6 is a 65.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 43.4%.

Frequently Compared With IS 4367 40Ni6Cr4Mo3:
NF A35-565 100C6 UNI 11234 100Cr6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 EN 10028-2 10CrMo9-10
Match Breakdown
CHEMISTRY MATCH
65.1%
MECHANICAL MATCH
0%
OVERALL
43.4%
Specifications
Property IS 4367 40Ni6Cr4Mo3 IS 4367 07Cr4Mo6
Standard IS 4367:1991 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 <=0.12
Si (%) 0.10-0.35 0.15-0.60
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 1.25-1.75 <=0.30
Cr (%) 0.90-1.30 0.70-1.10
Mo (%) 0.20-0.35 0.45-0.65
S (%) <=0.035 <=0.035
P (%) <=0.035 <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 4367 40Ni6Cr4Mo3 IS 4367 07Cr4Mo6
Tensile Strength 900-1050 MPa 380-550 MPa
Yield Strength 700 MPa min 225 MPa min
Elongation >=15% >=19%
Izod Impact 55 J min 60 J min
Hardness 266-311 HB Not specified
Hardness (soft annealed) <=230 HB <=170 HB
Condition Hardened and tempered, ruling section up to 150 mm Normalised and tempered, ruling section up to 40 mm
Typical Applications
IS 4367 40Ni6Cr4Mo3
aircraft landing gear, high strength shafts, gears, axles, connecting rods, heavy engineering components
IS 4367 07Cr4Mo6
Not documented
Can IS 4367 40Ni6Cr4Mo3 Be Substituted With IS 4367 07Cr4Mo6?
IS 4367 40Ni6Cr4Mo3 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 4367 40Ni6Cr4Mo3
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5000–5200 mm (196.85–204.72 in)
IS 4367 07Cr4Mo6
No active listings currently.
On M-EX Right Now
IS 4367 40Ni6Cr4Mo3
2 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 4367 40Ni6Cr4Mo3 and IS 4367 07Cr4Mo6?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 4367 40Ni6Cr4Mo3 be substituted with IS 4367 07Cr4Mo6?
IS 4367 40Ni6Cr4Mo3 and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.